Oxidation Behavior of a Ti3AlC2/TiB2 Composite at 1000 degrees-1400 degrees C in Air
Li, Meishuan1; Li, Chao1,2; Li, Jingjing1; Zhou, Yanchun1
Corresponding AuthorLi, Meishuan(mshli@imr.ac.cn)
2010-02-01
Source PublicationJOURNAL OF THE AMERICAN CERAMIC SOCIETY
ISSN0002-7820
Volume93Issue:2Pages:554-560
AbstractThe oxidation behaviors of a Ti3AlC2/20(vol%)TiB2 composite, synthesized by means of in situ reactions of Ti, Al, graphite, and B4C powder mixtures under hot pressing, have been investigated at 1000 degrees-1400 degrees C in air. The Ti3AlC2/20TiB(2) composite followed the logarithmic oxidation law, and had a lower oxidation rate than the matrix Ti3AlC2. During the oxidation at 1000 degrees-1400 degrees C, a continuous Al2O3 formed on the composite, meanwhile other different oxides formed on the top surface of the Al2O3 layer, depending on the oxidation temperature: discontinuous alpha-TiO2 at below 1200 degrees C, mixture of Al2TiO5 and TiO2 at 1300 degrees C, and continuous Al2TiO5 at 1400 degrees C. The selective oxidation of Al occurred at the oxide/substrate interface through inward diffusion of oxygen, and TiO2 overgrew the Al2O3 layer to form coarse grains through outward diffusion of titanium ions. When the temperature was above 1280 degrees C, Al2TiO5 appeared due to a eutectic reaction between TiO2 and Al2O3. The incorporation of TiB2 promoted the generation of great numbers of voids at the Al2O3/substrate interface and in the Al2O3 inner layer, which is proposed as being the main reason for the Ti3AlC2/20TiB(2) composite to follow a logarithmic oxidation law.
Funding OrganizationNational Science Foundation of China
DOI10.1111/j.1551-2916.2009.03434.x
Indexed BySCI
Language英语
Funding ProjectNational Science Foundation of China[50771099]
WOS Research AreaMaterials Science
WOS SubjectMaterials Science, Ceramics
WOS IDWOS:000274176500045
PublisherWILEY-BLACKWELL
Citation statistics
Cited Times:5[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/102823
Collection中国科学院金属研究所
Corresponding AuthorLi, Meishuan
Affiliation1.Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang, Peoples R China
2.Liaoning Univ, Coll Light Ind, Shenyang 110036, Peoples R China
Recommended Citation
GB/T 7714
Li, Meishuan,Li, Chao,Li, Jingjing,et al. Oxidation Behavior of a Ti3AlC2/TiB2 Composite at 1000 degrees-1400 degrees C in Air[J]. JOURNAL OF THE AMERICAN CERAMIC SOCIETY,2010,93(2):554-560.
APA Li, Meishuan,Li, Chao,Li, Jingjing,&Zhou, Yanchun.(2010).Oxidation Behavior of a Ti3AlC2/TiB2 Composite at 1000 degrees-1400 degrees C in Air.JOURNAL OF THE AMERICAN CERAMIC SOCIETY,93(2),554-560.
MLA Li, Meishuan,et al."Oxidation Behavior of a Ti3AlC2/TiB2 Composite at 1000 degrees-1400 degrees C in Air".JOURNAL OF THE AMERICAN CERAMIC SOCIETY 93.2(2010):554-560.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Li, Meishuan]'s Articles
[Li, Chao]'s Articles
[Li, Jingjing]'s Articles
Baidu academic
Similar articles in Baidu academic
[Li, Meishuan]'s Articles
[Li, Chao]'s Articles
[Li, Jingjing]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Li, Meishuan]'s Articles
[Li, Chao]'s Articles
[Li, Jingjing]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.