| Effects of Re-Melting Processes on the Tensile Properties of K452 Alloy at High Temperature | |
| Yang Jinxia1; Xu Futao1; Zhou Donglin2; Sun Yuan1; Hou Xingyu1; Cui Chuanyong1 | |
| Corresponding Author | Yang Jinxia(jxyang@imr.ac.cn) |
| 2017-06-01 | |
| Source Publication | ACTA METALLURGICA SINICA
 |
| ISSN | 0412-1961 |
| Volume | 53Issue:6Pages:703-708 |
| Abstract | K452 alloy is a nickel-based cast superalloy having the good tensile properties at high temperature and excellent corrosion resistance. It has been applied as a blade material of engines when environmental temperature is not above 950 degrees C. It is found that the tensile properties of the alloy have become more scattered and unstable although its chemical compositions are not changed. Hence, the tensile properties of the alloy were studied in order to increase its stability at high temperature and improve its applied properties. Tensile specimens were prepared using the different re-melting processes. Tensile tests were done at 900 degrees C. When the pouring temperature was 1430 degrees C, tensile properties were not only lower than expected, but also had great degree of dispersion, i.e., the vales of ultimate strengths changed in the range of 410 MPa and 510 MPa, and the elongations changed in the range of 3.5% and 22.0%, the average contents of O and N were the highest among three tested conditions. The highest N content was 0.0028%. And the shrinkage area was higher than those in other two re-melting processes. When the pouring temperature was 1500 degrees C, the tensile properties were improved, and their changing scopes became small, the average contents of O and N decreased, the shrinkage area decreased. When the refining temperature was 1590 degrees C and the holding time was 5 min, both average contents of O and N were decreased greatly, the shrinkage was not seen in the fracture surfaces. And the tensile properties were improved. Furthermore, their changing scopes were very small. |
| Keyword | superalloy tensile property shrinkage |
| Funding Organization | National Natural Science Foundation of China |
| DOI | 10.11900/0412.1961.2016.00286 |
| Indexed By | SCI |
| Language | 英语 |
| Funding Project | National Natural Science Foundation of China[11332010] |
| WOS Research Area | Metallurgy & Metallurgical Engineering |
| WOS Subject | Metallurgy & Metallurgical Engineering |
| WOS ID | WOS:000405561500008 |
| Publisher | SCIENCE PRESS |
| Citation statistics | |
| Document Type | 期刊论文 |
| Identifier | http://ir.imr.ac.cn/handle/321006/124707 |
| Collection | 中国科学院金属研究所 |
| Corresponding Author | Yang Jinxia |
| Affiliation | 1.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China 2.Harbin Dongan Engine Grp Corp LTD, Harbin 150066, Peoples R China |
| Recommended Citation GB/T 7714 | Yang Jinxia,Xu Futao,Zhou Donglin,et al. Effects of Re-Melting Processes on the Tensile Properties of K452 Alloy at High Temperature[J]. ACTA METALLURGICA SINICA,2017,53(6):703-708. |
| APA | Yang Jinxia,Xu Futao,Zhou Donglin,Sun Yuan,Hou Xingyu,&Cui Chuanyong.(2017).Effects of Re-Melting Processes on the Tensile Properties of K452 Alloy at High Temperature.ACTA METALLURGICA SINICA,53(6),703-708. |
| MLA | Yang Jinxia,et al."Effects of Re-Melting Processes on the Tensile Properties of K452 Alloy at High Temperature".ACTA METALLURGICA SINICA 53.6(2017):703-708. |
| Files in This Item: | There are no files associated with this item. | |||||
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment