THE CONCENTRATION OF HYDROGEN AT CRACK TIP OF AUSTENITIC STAINLESS-STEEL AFTER STRESS-CORROSION AND POLARIZATION
QIAO, LJ; HSIAO, CM; CHU, WY; CHEN, L; LIU, SW; ZOU, JJ
Corresponding AuthorQIAO, LJ()
1988-05-01
Source PublicationSCRIPTA METALLURGICA
ISSN0036-9748
Volume22Issue:5Pages:627-630
Indexed BySCI
Language英语
WOS Research AreaMetallurgy & Metallurgical Engineering
WOS SubjectMetallurgy & Metallurgical Engineering
WOS IDWOS:A1988N172400010
PublisherPERGAMON-ELSEVIER SCIENCE LTD
Citation statistics
Cited Times:25[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/126145
Collection中国科学院金属研究所
Corresponding AuthorQIAO, LJ
AffiliationCHINESE ACAD SCI,INST MET RES,SHANGHAI,PEOPLES R CHINA
Recommended Citation
GB/T 7714
QIAO, LJ,HSIAO, CM,CHU, WY,et al. THE CONCENTRATION OF HYDROGEN AT CRACK TIP OF AUSTENITIC STAINLESS-STEEL AFTER STRESS-CORROSION AND POLARIZATION[J]. SCRIPTA METALLURGICA,1988,22(5):627-630.
APA QIAO, LJ,HSIAO, CM,CHU, WY,CHEN, L,LIU, SW,&ZOU, JJ.(1988).THE CONCENTRATION OF HYDROGEN AT CRACK TIP OF AUSTENITIC STAINLESS-STEEL AFTER STRESS-CORROSION AND POLARIZATION.SCRIPTA METALLURGICA,22(5),627-630.
MLA QIAO, LJ,et al."THE CONCENTRATION OF HYDROGEN AT CRACK TIP OF AUSTENITIC STAINLESS-STEEL AFTER STRESS-CORROSION AND POLARIZATION".SCRIPTA METALLURGICA 22.5(1988):627-630.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[QIAO, LJ]'s Articles
[HSIAO, CM]'s Articles
[CHU, WY]'s Articles
Baidu academic
Similar articles in Baidu academic
[QIAO, LJ]'s Articles
[HSIAO, CM]'s Articles
[CHU, WY]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[QIAO, LJ]'s Articles
[HSIAO, CM]'s Articles
[CHU, WY]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.