| Heat-affected zone crack healing in IN939 repaired joints using hot isostatic pressing | |
| Xie, Jilin1,2; Ma, Yingche1; Xing, Weiwei1; Zhang, Long1; Ou, Meiqiong1,2; Liu, Kui1 | |
| Corresponding Author | Ma, Yingche(ycma@imr.ac.cn) |
| 2018-05-01 | |
| Source Publication | WELDING IN THE WORLD
 |
| ISSN | 0043-2288 |
| Volume | 62Issue:3Pages:471-479 |
| Abstract | Simulation defects in IN 939 superalloy were repaired by gas tungsten arc welding (GTAW) using Nimonic C263 as filler metal. The microstructures and chemical compositions of fusion zone under the condition of as-welded and post-weld heat treatment (PWHT) were investigated by optical microscopy (OM), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and electron probe X-ray microanalysis (EPMA). Moreover, the liquation cracking and strain age cracking in heat-affected zone (HAZ) were characterized as well. Post-weld hot isostatic pressing (HIP) was also applied to heal the HAZ cracks. The results show that elements segregation at as-welded joints could be significantly reduced by PWHT. HAZ cracks consisted of liquation cracking and strain age cracking. The liquation cracking was shorter than the strain age cracking. HIP is an effective way to heal the cracks in the repaired joints especially for liquation cracking. Though the strain age cracking can be healed by HIP. the healed trace concentrated with Al, Ti, B, and Zr elements can still be detected. Post-weld HIP is a necessary process to obtain crack-fire joints. |
| Keyword | IN 939 superalloy Microstructure HAZ cracks HIP Crack healing |
| DOI | 10.1007/s40194-018-0579-5 |
| Indexed By | SCI |
| Language | 英语 |
| WOS Research Area | Metallurgy & Metallurgical Engineering |
| WOS Subject | Metallurgy & Metallurgical Engineering |
| WOS ID | WOS:000441244700003 |
| Publisher | SPRINGER HEIDELBERG |
| Citation statistics | |
| Document Type | 期刊论文 |
| Identifier | http://ir.imr.ac.cn/handle/321006/128884 |
| Collection | 中国科学院金属研究所 |
| Corresponding Author | Ma, Yingche |
| Affiliation | 1.Chinese Acad Sci, Inst Met Res, Shenyang, Liaoning, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Hefei, Anhui, Peoples R China |
| Recommended Citation GB/T 7714 | Xie, Jilin,Ma, Yingche,Xing, Weiwei,et al. Heat-affected zone crack healing in IN939 repaired joints using hot isostatic pressing[J]. WELDING IN THE WORLD,2018,62(3):471-479. |
| APA | Xie, Jilin,Ma, Yingche,Xing, Weiwei,Zhang, Long,Ou, Meiqiong,&Liu, Kui.(2018).Heat-affected zone crack healing in IN939 repaired joints using hot isostatic pressing.WELDING IN THE WORLD,62(3),471-479. |
| MLA | Xie, Jilin,et al."Heat-affected zone crack healing in IN939 repaired joints using hot isostatic pressing".WELDING IN THE WORLD 62.3(2018):471-479. |
| Files in This Item: | There are no files associated with this item. | |||||
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment