Effects of normal load on fretting corrosion fatigue of Alloy 690 in 285 degrees C pure water
Liao, Jiapeng1,2; Tan, Jibo1; Wu, Xinqiang1; Tang, Lichen3; Qian, Hao3; Xie, Yongcheng3
Corresponding AuthorWu, Xinqiang(xqwu@imr.ac.cn)
2018-08-15
Source PublicationCORROSION SCIENCE
ISSN0010-938X
Volume141Pages:158-167
AbstractFretting corrosion fatigue behaviour of Alloy 690 was investigated in 285 degrees C pure water under different normal loads. With increasing the normal load applied, the fatigue life decreased, more severe surface damage and subsurface deformation were observed. The effects of normal loads on crack characteristics on the longitudinal sections across the fretting fatigue scars and corrosion fatigue fractures were examined. Possible influence of the normal loads on initiation and propagation mechanisms of the fretting corrosion fatigue cracks of Alloy 690 in high-temperature pure water are discussed.
KeywordAlloy SEM Fretting corrosion Corrosion fatigue High-temperature corrosion
Funding OrganizationNational Science and Technology Major Project ; National Natural Science Foundation of China ; Key Programs of the Chinese Academy of Sciences (Research on the Development of Nuclear Power Materials and Service Security Technology) ; Innovation Fund of Institute of Metal Research, Chinese Academy of Sciences
DOI10.1016/j.corsci.2018.07.010
Indexed BySCI
Language英语
Funding ProjectNational Science and Technology Major Project[2017ZX06002003-004-002] ; National Natural Science Foundation of China[51671201] ; Key Programs of the Chinese Academy of Sciences (Research on the Development of Nuclear Power Materials and Service Security Technology)[ZDRW-CN-2017-1] ; Innovation Fund of Institute of Metal Research, Chinese Academy of Sciences[SCJJ-2013-ZD-02]
WOS Research AreaMaterials Science ; Metallurgy & Metallurgical Engineering
WOS SubjectMaterials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
WOS IDWOS:000441682000017
PublisherPERGAMON-ELSEVIER SCIENCE LTD
Citation statistics
Cited Times:5[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/129064
Collection中国科学院金属研究所
Corresponding AuthorWu, Xinqiang
Affiliation1.Chinese Acad Sci, Inst Met Res, Liaoning Key Lab Safety & Assessment Tech Nucl Ma, CAS Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Liaoning, Peoples R China
2.Univ Sci & Technol China, Sch Mat Sci & Engn, Hefei 230026, Anhui, Peoples R China
3.Shanghai Nucl Engn Res & Design Inst, Shanghai 200233, Peoples R China
Recommended Citation
GB/T 7714
Liao, Jiapeng,Tan, Jibo,Wu, Xinqiang,et al. Effects of normal load on fretting corrosion fatigue of Alloy 690 in 285 degrees C pure water[J]. CORROSION SCIENCE,2018,141:158-167.
APA Liao, Jiapeng,Tan, Jibo,Wu, Xinqiang,Tang, Lichen,Qian, Hao,&Xie, Yongcheng.(2018).Effects of normal load on fretting corrosion fatigue of Alloy 690 in 285 degrees C pure water.CORROSION SCIENCE,141,158-167.
MLA Liao, Jiapeng,et al."Effects of normal load on fretting corrosion fatigue of Alloy 690 in 285 degrees C pure water".CORROSION SCIENCE 141(2018):158-167.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Liao, Jiapeng]'s Articles
[Tan, Jibo]'s Articles
[Wu, Xinqiang]'s Articles
Baidu academic
Similar articles in Baidu academic
[Liao, Jiapeng]'s Articles
[Tan, Jibo]'s Articles
[Wu, Xinqiang]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Liao, Jiapeng]'s Articles
[Tan, Jibo]'s Articles
[Wu, Xinqiang]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.