Effects of normal load on fretting corrosion fatigue of Alloy 690 in 285 degrees C pure water

doi:10.1016/j.corsci.2018.07.010

IMR OpenIR

	Effects of normal load on fretting corrosion fatigue of Alloy 690 in 285 degrees C pure water
	Liao, Jiapeng 1,2; Tan, Jibo 1; Wu, Xinqiang 1; Tang, Lichen 3; Qian, Hao 3; Xie, Yongcheng 3
通讯作者	Wu, Xinqiang(xqwu@imr.ac.cn)
	2018-08-15
发表期刊	CORROSION SCIENCE
ISSN	0010-938X
卷号	141 页码:158-167
摘要	Fretting corrosion fatigue behaviour of Alloy 690 was investigated in 285 degrees C pure water under different normal loads. With increasing the normal load applied, the fatigue life decreased, more severe surface damage and subsurface deformation were observed. The effects of normal loads on crack characteristics on the longitudinal sections across the fretting fatigue scars and corrosion fatigue fractures were examined. Possible influence of the normal loads on initiation and propagation mechanisms of the fretting corrosion fatigue cracks of Alloy 690 in high-temperature pure water are discussed.
关键词	Alloy SEM Fretting corrosion Corrosion fatigue High-temperature corrosion
资助者	National Science and Technology Major Project ; National Natural Science Foundation of China ; Key Programs of the Chinese Academy of Sciences (Research on the Development of Nuclear Power Materials and Service Security Technology) ; Innovation Fund of Institute of Metal Research, Chinese Academy of Sciences
DOI	10.1016/j.corsci.2018.07.010
收录类别	SCI
语种	英语
资助项目	National Science and Technology Major Project[2017ZX06002003-004-002] ; National Natural Science Foundation of China[51671201] ; Key Programs of the Chinese Academy of Sciences (Research on the Development of Nuclear Power Materials and Service Security Technology)[ZDRW-CN-2017-1] ; Innovation Fund of Institute of Metal Research, Chinese Academy of Sciences[SCJJ-2013-ZD-02]
WOS研究方向	Materials Science ; Metallurgy & Metallurgical Engineering
WOS类目	Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
WOS记录号	WOS:000441682000017
出版者	PERGAMON-ELSEVIER SCIENCE LTD
引用统计	被引频次：14[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/129064
专题	中国科学院金属研究所
通讯作者	Wu, Xinqiang
作者单位	1.Chinese Acad Sci, Inst Met Res, Liaoning Key Lab Safety & Assessment Tech Nucl Ma, CAS Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Liaoning, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Hefei 230026, Anhui, Peoples R China 3.Shanghai Nucl Engn Res & Design Inst, Shanghai 200233, Peoples R China
推荐引用方式 GB/T 7714	Liao, Jiapeng,Tan, Jibo,Wu, Xinqiang,et al. Effects of normal load on fretting corrosion fatigue of Alloy 690 in 285 degrees C pure water[J]. CORROSION SCIENCE,2018,141:158-167.
APA	Liao, Jiapeng,Tan, Jibo,Wu, Xinqiang,Tang, Lichen,Qian, Hao,&Xie, Yongcheng.(2018).Effects of normal load on fretting corrosion fatigue of Alloy 690 in 285 degrees C pure water.CORROSION SCIENCE,141,158-167.
MLA	Liao, Jiapeng,et al."Effects of normal load on fretting corrosion fatigue of Alloy 690 in 285 degrees C pure water".CORROSION SCIENCE 141(2018):158-167.