The microstructure and tribological behavior of a pre-cold-deformed 0.90 % nitrogen containing stainless steel

doi:10.1002/mawe.201700142

IMR OpenIR

	The microstructure and tribological behavior of a pre-cold-deformed 0.90 % nitrogen containing stainless steel
	Zhao, H.1,2; Ren, Y.2; Dong, J.2; Yang, K.2
通讯作者	Ren, Y.(ybren@imr.ac.cn)
	2018-12-01
发表期刊	MATERIALWISSENSCHAFT UND WERKSTOFFTECHNIK
ISSN	0933-5137
卷号	49 期号:12 页码:1439-1448
摘要	The microstructure of a 0.90 % nitrogen containing stainless steel pre-deformed by cold rolling was analyzed using optical microscopy, transmission electron microscopy and X-ray diffraction; Then the tribological behavior of nitrogen containing stainless steel was investigated using sliding wear method in air and in sodium chloride solutions and the worn surface was observed by a scanning electron microscopy. The results indicated that nitrogen containing stainless steel possessed stable single-phase austenite and the number of mechanical twins increased with increasing cold deformation. In dry wear tests, when the GCr15 bearing steel ball and 304 stainless steel ball acted as the counterpart, the wear resistance of nitrogen containing stainless steel decreased gradually and kept nearly the same, respectively, with increasing cold deformation. The corrosion wear resistance of nitrogen containing stainless steel was improved gradually by cold deformation in the 0.9 % sodium chloride solution and 3.5 % sodium chloride solution, while their friction coefficients were nearly equal.
关键词	Nitrogen containing stainless steel wear rate cold deformation friction coefficient microstructure
资助者	National Natural Science Foundation of China ; National Basic Research Program of China (973 Program)
DOI	10.1002/mawe.201700142
收录类别	SCI
语种	英语
资助项目	National Natural Science Foundation of China[31370976] ; National Basic Research Program of China (973 Program)[2012CB619101]
WOS研究方向	Materials Science
WOS类目	Materials Science, Multidisciplinary
WOS记录号	WOS:000453236700002
出版者	WILEY-V C H VERLAG GMBH
引用统计	被引频次：5[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/130668
专题	中国科学院金属研究所
通讯作者	Ren, Y.
作者单位	1.AECC Guizhou Liyang Aviat Power Co LTD, Guiyang 550014, Guizhou, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China
推荐引用方式 GB/T 7714	Zhao, H.,Ren, Y.,Dong, J.,et al. The microstructure and tribological behavior of a pre-cold-deformed 0.90 % nitrogen containing stainless steel[J]. MATERIALWISSENSCHAFT UND WERKSTOFFTECHNIK,2018,49(12):1439-1448.
APA	Zhao, H.,Ren, Y.,Dong, J.,&Yang, K..(2018).The microstructure and tribological behavior of a pre-cold-deformed 0.90 % nitrogen containing stainless steel.MATERIALWISSENSCHAFT UND WERKSTOFFTECHNIK,49(12),1439-1448.
MLA	Zhao, H.,et al."The microstructure and tribological behavior of a pre-cold-deformed 0.90 % nitrogen containing stainless steel".MATERIALWISSENSCHAFT UND WERKSTOFFTECHNIK 49.12(2018):1439-1448.