Effect of Ta particles on the fracture behavior of notched bulk metallic glass composites | |
Pan, J.; Lin, Y.; Zhang, J.; Huang, W.; Li, Y. | |
Corresponding Author | Pan, J.(jiepan@imr.ac.cn) ; Li, Y.(liyi@imr.ac.cn) |
2019-03-01 | |
Source Publication | INTERMETALLICS
![]() |
ISSN | 0966-9795 |
Volume | 106Pages:1-6 |
Abstract | The existence of second phase usually promotes the formation of multiple shear bands under uniaxial loading, leading to the apparent strain hardening and enhanced plasticity in bulk metallic glasses (BMGs). However, the effect of second phase on the fracture behavior of BMGs has been rarely investigated when shear banding is suppressed. In this work, the effect of Ta particles on the fracture behavior of notched bulk metallic glass composites (BMGCs) was investigated, where shear banding is suppressed due to the introduction of high triaxial stress state. With an increase in the volume fraction of Ta particles from 0 to 3.3%, the fracture strength significantly decreases from 2.70 to 1.20 GPa. Different from the vein-like patterns caused by shear banding, the fracture surface of notched BMGCs displays numerous equiaxed dimples and micro-cracks, indicating that voids nucleation and coalescence govern the fracture process. Due to the relatively weak bonding of the interface and the mechanical incompatibility between Ta particles and amorphous matrix, voids tend to nucleate at the interface during tensile deformation, giving rise to a reduction in the fracture strength of BMGCs. |
Keyword | Bulk metallic glass composite Fracture strength Triaxial stress state Dimples |
Funding Organization | National Natural Science Foundation of China |
DOI | 10.1016/j.intermet.2018.12.005 |
Indexed By | SCI |
Language | 英语 |
Funding Project | National Natural Science Foundation of China[51871217] ; National Natural Science Foundation of China[51401220] ; National Natural Science Foundation of China[51471165] |
WOS Research Area | Chemistry ; Materials Science ; Metallurgy & Metallurgical Engineering |
WOS Subject | Chemistry, Physical ; Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering |
WOS ID | WOS:000457815700001 |
Publisher | ELSEVIER SCI LTD |
Citation statistics | |
Document Type | 期刊论文 |
Identifier | http://ir.imr.ac.cn/handle/321006/131545 |
Collection | 中国科学院金属研究所 |
Corresponding Author | Pan, J.; Li, Y. |
Affiliation | Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Liaoning, Peoples R China |
Recommended Citation GB/T 7714 | Pan, J.,Lin, Y.,Zhang, J.,et al. Effect of Ta particles on the fracture behavior of notched bulk metallic glass composites[J]. INTERMETALLICS,2019,106:1-6. |
APA | Pan, J.,Lin, Y.,Zhang, J.,Huang, W.,&Li, Y..(2019).Effect of Ta particles on the fracture behavior of notched bulk metallic glass composites.INTERMETALLICS,106,1-6. |
MLA | Pan, J.,et al."Effect of Ta particles on the fracture behavior of notched bulk metallic glass composites".INTERMETALLICS 106(2019):1-6. |
Files in This Item: | There are no files associated with this item. |
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment