| Hot Corrosion Behavior of SiO2-Al2O3-Glass Composite Coating on Ti-47Al-2Cr-2Nb Alloy: Diffusion Barrier for S and Cl | |
| Li, Wen-Bo1; Liu, Lan-Lan1; Yang, Ying-Fei2; Zhu, Sheng-Long3; Wang, Fu-Hui3 | |
| Corresponding Author | Yang, Ying-Fei(yfyang@jnu.edu.cn) |
| 2019-05-01 | |
| Source Publication | ACTA METALLURGICA SINICA-ENGLISH LETTERS
 |
| ISSN | 1006-7191 |
| Volume | 32Issue:5Pages:599-606 |
| Abstract | Type I hot corrosion behavior of SiO2-Al2O3-glass composite coating based on Ti-47Al-2Cr-2Nb substrate was investigated in the mixture salt of 25wt%NaCl+75wt%Na2SO4 at 850 degrees C. The results showed that there was a bidirectional ion exchange between composite coating and the film of mixed salts, and the sodium ion in the molten salts penetrated into the glass matrix of composite coating, while the potassium ion in the glass matrix dissolved into the molten salts. A decrease in hot corrosion rate was achieved for the coated alloy in comparison with the bared substrate due to the composite coating acting as a diffusion barrier to sulfur and chlorine and preventing the molten salts from diffusing to the coating/alloy interface during the hot corrosion exposure. Additionally, the composite coating decreased the oxygen partial pressure at the coating/alloy interface and promoted the selective oxidation of Al to form a protective Al2O3 layer. |
| Keyword | Corrosion Composite coating Ti-47Al-2Cr-2Nb alloy Diffusion |
| Funding Organization | National Natural Science Foundation of China ; National High Technology Research and Development Program of China (863 Program) |
| DOI | 10.1007/s40195-018-0842-1 |
| Indexed By | SCI |
| Language | 英语 |
| Funding Project | National Natural Science Foundation of China[51201171] ; National High Technology Research and Development Program of China (863 Program)[2012AA03A512] |
| WOS Research Area | Metallurgy & Metallurgical Engineering |
| WOS Subject | Metallurgy & Metallurgical Engineering |
| WOS ID | WOS:000463780700007 |
| Publisher | CHINESE ACAD SCIENCES, INST METAL RESEARCH |
| Citation statistics | |
| Document Type | 期刊论文 |
| Identifier | http://ir.imr.ac.cn/handle/321006/132945 |
| Collection | 中国科学院金属研究所 |
| Corresponding Author | Yang, Ying-Fei |
| Affiliation | 1.Hunan Elect Power Co Ltd, Changsha, Hunan, Peoples R China 2.Jinan Univ, Inst Adv Wear & Corros Resistant & Funct Mat, Guangzhou 510632, Guangdong, Peoples R China 3.Chinese Acad Sci, Inst Met Res, Lab Corros & Protect, Shenyang 110016, Liaoning, Peoples R China |
| Recommended Citation GB/T 7714 | Li, Wen-Bo,Liu, Lan-Lan,Yang, Ying-Fei,et al. Hot Corrosion Behavior of SiO2-Al2O3-Glass Composite Coating on Ti-47Al-2Cr-2Nb Alloy: Diffusion Barrier for S and Cl[J]. ACTA METALLURGICA SINICA-ENGLISH LETTERS,2019,32(5):599-606. |
| APA | Li, Wen-Bo,Liu, Lan-Lan,Yang, Ying-Fei,Zhu, Sheng-Long,&Wang, Fu-Hui.(2019).Hot Corrosion Behavior of SiO2-Al2O3-Glass Composite Coating on Ti-47Al-2Cr-2Nb Alloy: Diffusion Barrier for S and Cl.ACTA METALLURGICA SINICA-ENGLISH LETTERS,32(5),599-606. |
| MLA | Li, Wen-Bo,et al."Hot Corrosion Behavior of SiO2-Al2O3-Glass Composite Coating on Ti-47Al-2Cr-2Nb Alloy: Diffusion Barrier for S and Cl".ACTA METALLURGICA SINICA-ENGLISH LETTERS 32.5(2019):599-606. |
| Files in This Item: | There are no files associated with this item. | |||||
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment