| Stress rupture properties and deformation mechanisms of K4750 alloy at the range of 650 degrees C to 800 degrees C | |
| Ou, Meiqiong; Ma, Yingche; Xing, Weiwei; Hao, Xianchao; Chen, Bo; Ding, Leilei; Liu, Kui | |
| Corresponding Author | Ma, Yingche(ycma@imr.ac.cn) ; Liu, Kui(kliu@imr.ac.cn) |
| 2019-07-01 | |
| Source Publication | JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
 |
| ISSN | 1005-0302 |
| Volume | 35Issue:7Pages:1270-1277 |
| Abstract | The stress rupture properties and deformation mechanisms of K4750 alloy at 650 degrees C, 700 degrees C, 750 degrees C and 800 degrees C were investigated. As the decrease of temperature and stress, the stress rupture life gradually increased. A Larson-Miller Parameter (LMP) method was used for analyzing the stress rupture life under different conditions. The linear fitting formula between stress (sigma) and LMP was derived as sigma = 3166.455 - 119.969 x LMP and the fitting coefficient was 0.98. After testing, the dislocation configurations of all stress rupture samples were investigated by transmission electron microscopy (TEM). The temperature and stress had a significant impact on the deformation mechanism, thereby affected the stress rupture life of K4750 alloy. As the increasing stress at a given temperature, the deformation mechanism gradually transformed from Orowan looping to stacking fault shearing. Based on experimental results, the threshold stress at 650 degrees C, 700 degrees C, 750 degrees C and 800 degrees C for the transition of deformation mechanism was estimated to be about 650 MPa, 530 MPa, 430 MPa and 350 MPa, respectively. Below the threshold stress, gamma' phase effectively hindered dislocation motion by Orowan looping mechanism, K4750 alloy had a long stress rupture life. Slightly above the threshold stress, Orowan looping combining stacking fault shearing was the dominant mechanism, the stress rupture life decreased. As the further increase of stress, stacking fault shearing acted as the dominant deformation mechanism, the resistance to dislocation motion decreased rapidly, so the stress rupture life reduced significantly. (C) 2019 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology. |
| Keyword | Nickel based superalloy Stress rupture properties Dislocation Deformation mechanisms Transmission electron microscopy |
| DOI | 10.1016/j.jmst.2019.03.002 |
| Indexed By | SCI |
| Language | 英语 |
| WOS Research Area | Materials Science ; Metallurgy & Metallurgical Engineering |
| WOS Subject | Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering |
| WOS ID | WOS:000466369600008 |
| Publisher | JOURNAL MATER SCI TECHNOL |
| Citation statistics | |
| Document Type | 期刊论文 |
| Identifier | http://ir.imr.ac.cn/handle/321006/133593 |
| Collection | 中国科学院金属研究所 |
| Corresponding Author | Ma, Yingche; Liu, Kui |
| Affiliation | Chinese Acad Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China |
| Recommended Citation GB/T 7714 | Ou, Meiqiong,Ma, Yingche,Xing, Weiwei,et al. Stress rupture properties and deformation mechanisms of K4750 alloy at the range of 650 degrees C to 800 degrees C[J]. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,2019,35(7):1270-1277. |
| APA | Ou, Meiqiong.,Ma, Yingche.,Xing, Weiwei.,Hao, Xianchao.,Chen, Bo.,...&Liu, Kui.(2019).Stress rupture properties and deformation mechanisms of K4750 alloy at the range of 650 degrees C to 800 degrees C.JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,35(7),1270-1277. |
| MLA | Ou, Meiqiong,et al."Stress rupture properties and deformation mechanisms of K4750 alloy at the range of 650 degrees C to 800 degrees C".JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY 35.7(2019):1270-1277. |
| Files in This Item: | There are no files associated with this item. | |||||
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment