Corrosion behavior of copper T2 and brass H62 in simulated Nansha marine atmosphere

doi:10.1016/j.jmst.2019.04.024

IMR OpenIR

	Corrosion behavior of copper T2 and brass H62 in simulated Nansha marine atmosphere
	Lu, Xiao 1,2; Liu, Yuwei 1,2; Liu, Miaoran 2,3; Wang, Zhenyao 1,2
通讯作者	Wang, Zhenyao(zhywang@imr.ac.cn)
	2019-09-01
发表期刊	JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
ISSN	1005-0302
卷号	35 期号:9 页码:1831-1839
摘要	The accelerated corrosion behavior of copper T2 and brass H62 exposed in simulated Nansha marine atmosphere for different periods were investigated by weight loss method, SEM. XRD and potentiodynamic polarization measurements. The results indicate that copper T2 and brass H62 underwent severe corrosion, and the final corrosion rates at 32 days of exposure were 0.24 mu m/d and 0.10 mu m/d, respectively. Moreover, the overall corrosion type of copper T2 was uniform and the corrosion products Cu2O and Cu2Cl(OH)(3) played a vital role in the corrosion rate of copper. While the dezincification corrosion with zinc preferential dissolution was obvious in brass H62. The predominant phases were the zinc-rich compounds Zn-5(OH)(8)Cl-2 center dot H2O, Zn-12(SO4)(3)Cl-3(OH)(15)center dot 5H(2)O and NaZn4(SO4)Cl(OH)(6)center dot 6H(2)O. There existed a large number of copper-rich holes with 20-50 pin depth beneath the corrosion product layer. (C) 2019 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.
关键词	Copper Brass Weight loss Nansha Atmospheric corrosion
资助者	National Natural Science Foundation of China ; Special Project of Chinese Academy of Sciences
DOI	10.1016/j.jmst.2019.04.024
收录类别	SCI
语种	英语
资助项目	National Natural Science Foundation of China[51671197] ; Special Project of Chinese Academy of Sciences[XDA130040502]
WOS研究方向	Materials Science ; Metallurgy & Metallurgical Engineering
WOS类目	Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
WOS记录号	WOS:000475870600004
出版者	JOURNAL MATER SCI TECHNOL
引用统计	被引频次：45[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/134837
专题	中国科学院金属研究所
通讯作者	Wang, Zhenyao
作者单位	1.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Liaoning, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China 3.Univ Chinese Acad Sci, Beijing 100049, Peoples R China
推荐引用方式 GB/T 7714	Lu, Xiao,Liu, Yuwei,Liu, Miaoran,et al. Corrosion behavior of copper T2 and brass H62 in simulated Nansha marine atmosphere[J]. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,2019,35(9):1831-1839.
APA	Lu, Xiao,Liu, Yuwei,Liu, Miaoran,&Wang, Zhenyao.(2019).Corrosion behavior of copper T2 and brass H62 in simulated Nansha marine atmosphere.JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,35(9),1831-1839.
MLA	Lu, Xiao,et al."Corrosion behavior of copper T2 and brass H62 in simulated Nansha marine atmosphere".JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY 35.9(2019):1831-1839.