| Enhancing Pitting Corrosion Resistance of Severely Cold-Worked High Nitrogen Austenitic Stainless Steel by Nitric Acid Passivation | |
| Li, Jun1,2; Wang, Qingchuan1; Yang, Yixun1,2; Wu, Zhiqiang3; Tan, Lili1; Ren, Yibin4; Yang, Ke1 | |
| Corresponding Author | Wang, Qingchuan(qcwang11s@imr.ac.cn) ; Yang, Ke(kyang@imr.ac.cn) |
| 2019-08-09 | |
| Source Publication | JOURNAL OF THE ELECTROCHEMICAL SOCIETY
 |
| ISSN | 0013-4651 |
| Volume | 166Issue:13Pages:C365-C374 |
| Abstract | Nitric acid passivation was applied on a high nitrogen austenitic stainless steel (HNS) to improve its pitting corrosion resistance which was obviously decreased by severe cold deformation. According to cyclic polarization and immersion results, the pitting corrosion resistance of HNS was found significantly improved by passivation and further enhanced with increase of the passivation temperature. In addition, severely cold-worked HNS passivated at 75 degrees C obtained much better pitting corrosion resistance, as its pit density was decreased by more than 50% compared with unpassivated solution-treated HNS. But cold-worked matrix showed a weaker passive film formation ability. Based on electrochemical results and XPS analyses, this improvement was attributed to the sharp increase of Cr oxide enrichment and the clear decrease of cation vacancy density of passive films. Besides, the dissolution of MnS inclusion had no effect on the improvement of pitting corrosion resistance. (C) 2019 The Electrochemical Society. |
| Funding Organization | National Natural Science Foundation of China |
| DOI | 10.1149/2.0211913jes |
| Indexed By | SCI |
| Language | 英语 |
| Funding Project | National Natural Science Foundation of China[51801220] |
| WOS Research Area | Electrochemistry ; Materials Science |
| WOS Subject | Electrochemistry ; Materials Science, Coatings & Films |
| WOS ID | WOS:000480517200001 |
| Publisher | ELECTROCHEMICAL SOC INC |
| Citation statistics | |
| Document Type | 期刊论文 |
| Identifier | http://ir.imr.ac.cn/handle/321006/135066 |
| Collection | 中国科学院金属研究所 |
| Corresponding Author | Wang, Qingchuan; Yang, Ke |
| Affiliation | 1.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Liaoning, Peoples R China 3.Northeastern Univ, State Key Lab Rolling & Automat, Shenyang 110819, Liaoning, Peoples R China 4.Shenyang Ligong Univ, Sch Mat Sci & Engn, Shenyang 110159, Liaoning, Peoples R China |
| Recommended Citation GB/T 7714 | Li, Jun,Wang, Qingchuan,Yang, Yixun,et al. Enhancing Pitting Corrosion Resistance of Severely Cold-Worked High Nitrogen Austenitic Stainless Steel by Nitric Acid Passivation[J]. JOURNAL OF THE ELECTROCHEMICAL SOCIETY,2019,166(13):C365-C374. |
| APA | Li, Jun.,Wang, Qingchuan.,Yang, Yixun.,Wu, Zhiqiang.,Tan, Lili.,...&Yang, Ke.(2019).Enhancing Pitting Corrosion Resistance of Severely Cold-Worked High Nitrogen Austenitic Stainless Steel by Nitric Acid Passivation.JOURNAL OF THE ELECTROCHEMICAL SOCIETY,166(13),C365-C374. |
| MLA | Li, Jun,et al."Enhancing Pitting Corrosion Resistance of Severely Cold-Worked High Nitrogen Austenitic Stainless Steel by Nitric Acid Passivation".JOURNAL OF THE ELECTROCHEMICAL SOCIETY 166.13(2019):C365-C374. |
| Files in This Item: | There are no files associated with this item. | |||||
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment