Formation and thermal stability of dual glass phases in the h-BN/SiO2/Yb-Si-Al-O composites
Chen, Juanjuan1,2; Chen, Jixin1
Corresponding AuthorChen, Jixin(jxchen@imr.ac.cn)
2020-02-01
Source PublicationJOURNAL OF THE EUROPEAN CERAMIC SOCIETY
ISSN0955-2219
Volume40Issue:2Pages:456-462
AbstractThe glass phases formation and microstructural evolution in the h-BN/SiO2/Yb-Si-Al-O composite were investigated. Owing to the introduction of Al2O3, SiO2 could transform into amorphous silica at a lower temperature (similar to 1600 degrees C). On the other hand, with increasing temperature, Al3+ gradually dissolved into ytterbium silicate (Yb2Si2O2) and then accelerated the formation of amorphous Yb-Si-Al-O glass phase. Up to 1880 degrees C, fine spherical Yb-Si-Al-O glass particles and irregular amorphous silica distributed uniformly, which contributes to the excellent mechanical properties of the composite. The thermal stability study disclosed that more [A1O(4)] units could effectively inhibit crystallization of the Yb-Si-Al-O glass phase, but mechanical properties of composite still decreased slowly with increasing the heat treatment temperature. For example, the flexural strength of the composite with 1.5 wt.% Al2O3 decreased from 297 +/- 30 to 284 +/- 22 MPa as the treatment temperature rose from 800 to 1200 degrees C.
Keywordh-BN based composite Dual glass phases Glass transition Microstructural evolution Thermal stability
Funding OrganizationNational Natural Science Foundation of China
DOI10.1016/j.jeurceramsoc.2019.10.028
Indexed BySCI
Language英语
Funding ProjectNational Natural Science Foundation of China[50802099] ; National Natural Science Foundation of China[51072201]
WOS Research AreaMaterials Science
WOS SubjectMaterials Science, Ceramics
WOS IDWOS:000498292100033
PublisherELSEVIER SCI LTD
Citation statistics
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/136193
Collection中国科学院金属研究所
Corresponding AuthorChen, Jixin
Affiliation1.Chinese Acad Sci, Inst Met Res, High Performance Ceram Div, Shenyang Natl Lab Mat Sci, Shenyang 110016, Liaoning, Peoples R China
2.Univ Chinese Acad Sci, Beijing 100049, Peoples R China
Recommended Citation
GB/T 7714
Chen, Juanjuan,Chen, Jixin. Formation and thermal stability of dual glass phases in the h-BN/SiO2/Yb-Si-Al-O composites[J]. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY,2020,40(2):456-462.
APA Chen, Juanjuan,&Chen, Jixin.(2020).Formation and thermal stability of dual glass phases in the h-BN/SiO2/Yb-Si-Al-O composites.JOURNAL OF THE EUROPEAN CERAMIC SOCIETY,40(2),456-462.
MLA Chen, Juanjuan,et al."Formation and thermal stability of dual glass phases in the h-BN/SiO2/Yb-Si-Al-O composites".JOURNAL OF THE EUROPEAN CERAMIC SOCIETY 40.2(2020):456-462.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Chen, Juanjuan]'s Articles
[Chen, Jixin]'s Articles
Baidu academic
Similar articles in Baidu academic
[Chen, Juanjuan]'s Articles
[Chen, Jixin]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Chen, Juanjuan]'s Articles
[Chen, Jixin]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.