Microstructure, Texture and Mechanical Property of TA32 Titanium Alloy Thick Plate
Cheng Chao1,2; Chen Zhiyong1,2; Qin Xushan3; Liu Jianrong1,2; Wang Qingjiang1,2
Corresponding AuthorChen Zhiyong(zhiyongchen@imr.ac.cn)
2020-02-11
Source PublicationACTA METALLURGICA SINICA
ISSN0412-1961
Volume56Issue:2Pages:193-202
AbstractTA32 alloy is a new near alpha titanium alloy designed by optimizing the alloy elements ratio based on a series of elements Ti-Al-Sn-Zr-Mo-Si-Nb-Ta which has less beta-stabilizing elements. This alloy has an excellent match of heat resistance and heat stability at 550 degrees C, and good short-term mechanical properties at 600 similar to 650 degrees C. TA32 titanium alloy thick plate can be applied to the key components in high temperature service of the hypersonic vehide. Due to the low deformation degree of thick plate during rolling process, the heterogeneity of microstructure, texture and mechanical properties of the thick plate increases. In order to provide theoretical basis and experimental basis for the subsequent optimization of mechanical properties of TA32 titanium alloy thick plate, the microstructure, texture and mechanical properties of this alloy with a thickness of 60 mm are investigated in this work. Results show that the microstructure of the as-received material is mainly composed of lamellar alpha grains with few retained thin beta layers, and the microstructure difference is not obvious from the surface to the center along the thickness direction of the plate no matter of the RD (rolling direction)-ND (normal direction) plane or the TD (transverse direction)-ND plane. Moreover, the rolling streamline can be obviously observed on the two planes. The morphology of alpha grains of the alloys presents either straight or wavy depending on their orientations with respect to the principal rolling directions. XRD results show that the as-received material has a typical T-type texture with c-axis of alpha phase approximately parallel to TD. At the same time, the <10<(1)over bar>0> poles are parallel to RD while <10<(1)over bar>1> poles present random distribution. As the c-axis gradually deviates from the TD of the surface to the center along the thickness direction of the plate, the Schmidt factors gradually increase, which is one of the main reasons for the gradual decrease of tensile strength; and the decrease of fraction of intragranular substructure from the surface to the center along the thickness direction is another important factor. The tensile properties have no obvious difference along the TD and RD at the same thickness position of the as-received material, but slightly worse along the ND. In addition, the influences of microstructure and texture on tensile properties are further clarified by adding two sets of heat treatment experiments (920 degrees C, 30 min, AC+600 degrees C, 5 h, AC; 950 degrees C, 30 min, AC+600 degrees C, 5 h, AC). The results show that the texture is the main factor affecting the tensile strength of TA32 titanium alloy plate at different positions under the condition of no obvious difference in microstructure. After double annealing, microstructure difference is the main factor affecting tensile strength.
KeywordTA32 titanium alloy thick plate microstructure texture mechanical property
DOI10.11900/0412.1961.2019.00226
Indexed BySCI
Language英语
WOS Research AreaMetallurgy & Metallurgical Engineering
WOS SubjectMetallurgy & Metallurgical Engineering
WOS IDWOS:000507327100007
PublisherSCIENCE PRESS
Citation statistics
Cited Times:2[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/136622
Collection中国科学院金属研究所
Corresponding AuthorChen Zhiyong
Affiliation1.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China
2.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China
3.Chinese Peoples Liberat Army, Unit 96901, Beijing 100094, Peoples R China
Recommended Citation
GB/T 7714
Cheng Chao,Chen Zhiyong,Qin Xushan,et al. Microstructure, Texture and Mechanical Property of TA32 Titanium Alloy Thick Plate[J]. ACTA METALLURGICA SINICA,2020,56(2):193-202.
APA Cheng Chao,Chen Zhiyong,Qin Xushan,Liu Jianrong,&Wang Qingjiang.(2020).Microstructure, Texture and Mechanical Property of TA32 Titanium Alloy Thick Plate.ACTA METALLURGICA SINICA,56(2),193-202.
MLA Cheng Chao,et al."Microstructure, Texture and Mechanical Property of TA32 Titanium Alloy Thick Plate".ACTA METALLURGICA SINICA 56.2(2020):193-202.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Cheng Chao]'s Articles
[Chen Zhiyong]'s Articles
[Qin Xushan]'s Articles
Baidu academic
Similar articles in Baidu academic
[Cheng Chao]'s Articles
[Chen Zhiyong]'s Articles
[Qin Xushan]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Cheng Chao]'s Articles
[Chen Zhiyong]'s Articles
[Qin Xushan]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.