The damage mechanism of 17vol.%SiCp/Al composite under uniaxial tensile stress

doi:10.1016/j.msea.2020.139274

IMR OpenIR

	The damage mechanism of 17vol.%SiCp/Al composite under uniaxial tensile stress
	Shen, Qiuyan 1,2; Yuan, Zhanwei 1,2; Liu, Huan 1,2; Zhang, Xuemin 1; Fu, Qinqin 3; Wang, Quanzhao 4
通讯作者	Yuan, Zhanwei(yuanyekingfly@163.com) ; Wang, Quanzhao(qzhwang@imr.ac.cn)
	2020-04-24
发表期刊	MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
ISSN	0921-5093
卷号	782 页码:11
摘要	In this paper, the deformation, fracture and damage behavior of SiCp/Al composites are studied by experiments and finite element analysis. The crack cracking process of the material was observed by in-situ tensile test, it was found that the composite first produced microcracks near the particles, and the cracks mainly spread to depth and then to both sides. It is determined by a tensile test that the fracture mechanism of the material is the tearing of the aluminum matrix and the peeling between the particles and the matrix. The tensile damage mechanism of the composite material in three directions (rolling direction, rolling transverse direction and rolling normal direction) and different strains were determined. It is found that in the process of tensile deformation, microcracks are first formed at the defects (voids) and weak interfaces, and many fine cracks converge together to form large cracks leading to the fracture of the material, during which a few particles fall off, but there is no particle fracture. The global and local tensile tests of the composites were simulated by finite element method, the results of the stress-strain state under different strains and the effects of particles on the materials are analyzed in detail, and the validity of the test results is determined.
关键词	SiCp/Al composite Damage behavior Fracture mechanism Finite element method Stress-state
资助者	China Postdoctoral Science Foundation ; National Science and Technology Major Project ; Fundamental Research Funds for the Central Universities, CHD
DOI	10.1016/j.msea.2020.139274
收录类别	SCI
语种	英语
资助项目	China Postdoctoral Science Foundation[2017M623084] ; National Science and Technology Major Project[2017-VII-0012-0107] ; Fundamental Research Funds for the Central Universities, CHD[310831172001] ; Fundamental Research Funds for the Central Universities, CHD[300102319101] ; Fundamental Research Funds for the Central Universities, CHD[300102310201]
WOS研究方向	Science & Technology - Other Topics ; Materials Science ; Metallurgy & Metallurgical Engineering
WOS类目	Nanoscience & Nanotechnology ; Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
WOS记录号	WOS:000525797900023
出版者	ELSEVIER SCIENCE SA
引用统计	被引频次：13[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/138235
专题	中国科学院金属研究所
通讯作者	Yuan, Zhanwei; Wang, Quanzhao
作者单位	1.Changan Univ, Sch Mat Sci & Engn, Xian 710061, Shaanxi, Peoples R China 2.Changan Univ, Lab Adv Technol & Equipment, Xian 710061, Shaanxi, Peoples R China 3.Xi An Jiao Tong Univ, Ctr Advancing Mat Performance Nanoscale CAMP Nano, HARCC, State Key Lab Mech Behav Mat, Xian 710049, Shaanxi, Peoples R China 4.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China
推荐引用方式 GB/T 7714	Shen, Qiuyan,Yuan, Zhanwei,Liu, Huan,et al. The damage mechanism of 17vol.%SiCp/Al composite under uniaxial tensile stress[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,2020,782:11.
APA	Shen, Qiuyan,Yuan, Zhanwei,Liu, Huan,Zhang, Xuemin,Fu, Qinqin,&Wang, Quanzhao.(2020).The damage mechanism of 17vol.%SiCp/Al composite under uniaxial tensile stress.MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,782,11.
MLA	Shen, Qiuyan,et al."The damage mechanism of 17vol.%SiCp/Al composite under uniaxial tensile stress".MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING 782(2020):11.