Friction stir welding of 2060-T8 Al-Li alloy. Part II: Tensile fracture behavior
Tao, Y.; Zhang, Z.; Yu, B. H.; Xue, P.; Ni, D. R.; Xiao, B. L.
Corresponding AuthorZhang, Z.(zhangzhen@imr.ac.cn)
2020-10-01
Source PublicationMATERIALS CHARACTERIZATION
ISSN1044-5803
Volume168Pages:11
AbstractFor friction stir welded (FSW) joints of conventional precipitation-hardened aluminum alloys, the lowest hardness zone (LHZ) was located at heat affected zone (HAZ) and determined the tensile fracture behavior with the fracture occurring at the LHZ. For FSW 2060-T8 joints, however, the LHZs were located at the nugget zone (NZ) under 400 rpm-200 mm/min, but at the HAZ under 800 rpm-200 mm/min, 1200 rpm-200 mm/min and 1200 rpm-50 mm/min. While the FSW 2060-T8 joints normally fractured along the LHZ under 400 rpm-200 mm/min and 1200 rpm-50 mm/min, abnormal fracture occurred at the thermo-mechanically affected zone (TMAZ) under 800 rpm-200 mm/min and 1200 rpm-200 mm/min. The FSW 2060-T8 joints with 800 rpm-200 mm/min and 1200 rpm-200 mm/min presented obvious diversity of crystal orientation and grain morphology, and subsequent deformation in the LHZs, the lower TMAZ and upper TMAZ. The large Schmid factor, coarse grains and delta'/beta' precipitates caused the preferential deformation and planar slip at the lower TMAZ, weakened the mechanical properties of the TMAZ, and therefore resulted in the abnormal failure at the TMAZ of FSW 2060-T8 joints under 800 rpm-200 mm/min and 1200 rpm-200 mm/min.
KeywordFriction stir welding Aluminum-lithium alloys Microstrucrure Microtexture Hardness Fracture behavior
Funding OrganizationNational Natural Science Foundation of China
DOI10.1016/j.matchar.2020.110507
Indexed BySCI
Language英语
Funding ProjectNational Natural Science Foundation of China[U1760201]
WOS Research AreaMaterials Science ; Metallurgy & Metallurgical Engineering
WOS SubjectMaterials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering ; Materials Science, Characterization & Testing
WOS IDWOS:000571731500005
PublisherELSEVIER SCIENCE INC
Citation statistics
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/140685
Collection中国科学院金属研究所
Corresponding AuthorZhang, Z.
AffiliationChinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China
Recommended Citation
GB/T 7714
Tao, Y.,Zhang, Z.,Yu, B. H.,et al. Friction stir welding of 2060-T8 Al-Li alloy. Part II: Tensile fracture behavior[J]. MATERIALS CHARACTERIZATION,2020,168:11.
APA Tao, Y.,Zhang, Z.,Yu, B. H.,Xue, P.,Ni, D. R.,&Xiao, B. L..(2020).Friction stir welding of 2060-T8 Al-Li alloy. Part II: Tensile fracture behavior.MATERIALS CHARACTERIZATION,168,11.
MLA Tao, Y.,et al."Friction stir welding of 2060-T8 Al-Li alloy. Part II: Tensile fracture behavior".MATERIALS CHARACTERIZATION 168(2020):11.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Tao, Y.]'s Articles
[Zhang, Z.]'s Articles
[Yu, B. H.]'s Articles
Baidu academic
Similar articles in Baidu academic
[Tao, Y.]'s Articles
[Zhang, Z.]'s Articles
[Yu, B. H.]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Tao, Y.]'s Articles
[Zhang, Z.]'s Articles
[Yu, B. H.]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.