Properties of Ti-Ni Pre-alloyed Powder Used for Electron Beam Melting
Ren Dechun1,2; Zhang Huibo1; Li Shujun1; Hou Wentao1; Wang Jian1; Jin Wei1; Yang Rui1
Corresponding AuthorJin Wei(wjin@imr.ac.cn)
2020-09-01
Source PublicationRARE METAL MATERIALS AND ENGINEERING
ISSN1002-185X
Volume49Issue:9Pages:3218-3224
AbstractThe properties of pre-alloyed powder have an important influence on the additive manufacturing process, especially for Ti-Ni alloys with special shape memory effects. However, there are limited reports on the studies for the variation of Ti-Ni pre-alloyed powder with heat treatment temperatures and number of thermal cycles. In this work, the phase transformation behavior, microstructure and phase composition of 53 similar to 106 mu m Ti-Ni pre-alloyed powder used for electron beam melting (EBM) were studied using the differential scanning calorimeter, X-ray diffraction, and scanning electron microscope. The results show that the powder has good particle size distribution, internal filling and spherical topography, and suitable for EBM process. The structure and composition become uniform, internal stress and dislocation are eliminated and crystal grain size grows with the increase of heat treatment temperature, which causes the original multi-step phase transformation to one-step phase transformation during the heating and cooling process after 550 degrees C and the phase transformation points maintain a stable state after 650 degrees C heat treatment. The phase composition is not changed during the heat treatment process and the powder has best sintering state at 750 degrees C. The phase composition, one-step phase transformation behavior and phase transformation points are all not changed for the powder during 750 degrees C thermal cycles test, indicating good thermal cycling stability. Ti-Ni solid samples with good surface condition are successfully prepared under 750 degrees C preheating temperature for bottom plate and powder layer.
KeywordTi-Ni pre-alloyed powder electron beam melting heat treatment thermal cycle phase transformation behavior
Indexed BySCI
Language英语
WOS Research AreaMaterials Science ; Metallurgy & Metallurgical Engineering
WOS SubjectMaterials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
WOS IDWOS:000576197200042
PublisherNORTHWEST INST NONFERROUS METAL RESEARCH
Citation statistics
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/140833
Collection中国科学院金属研究所
Corresponding AuthorJin Wei
Affiliation1.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China
2.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China
Recommended Citation
GB/T 7714
Ren Dechun,Zhang Huibo,Li Shujun,et al. Properties of Ti-Ni Pre-alloyed Powder Used for Electron Beam Melting[J]. RARE METAL MATERIALS AND ENGINEERING,2020,49(9):3218-3224.
APA Ren Dechun.,Zhang Huibo.,Li Shujun.,Hou Wentao.,Wang Jian.,...&Yang Rui.(2020).Properties of Ti-Ni Pre-alloyed Powder Used for Electron Beam Melting.RARE METAL MATERIALS AND ENGINEERING,49(9),3218-3224.
MLA Ren Dechun,et al."Properties of Ti-Ni Pre-alloyed Powder Used for Electron Beam Melting".RARE METAL MATERIALS AND ENGINEERING 49.9(2020):3218-3224.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Ren Dechun]'s Articles
[Zhang Huibo]'s Articles
[Li Shujun]'s Articles
Baidu academic
Similar articles in Baidu academic
[Ren Dechun]'s Articles
[Zhang Huibo]'s Articles
[Li Shujun]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Ren Dechun]'s Articles
[Zhang Huibo]'s Articles
[Li Shujun]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.