MICROSTRUCTURE AND ROOM TEMPERATURE COMPRESSION PROPERTIES OF Mg82.13Zn13.85Y4.02 ALLOY SOLIDIFIED UNDER SUPER-HIGH PRESSURE
Alternative TitleMICROSTRUCTURE AND ROOM TEMPERATURE COMPRESSION PROPERTIES OF Mg_(82.13)Zn_(13.85)Y_(4.02) ALLOY SOLIDIFIED UNDER SUPER-HIGH PRESSURE
Dong Yun1; Lin Xiaoping1; Xu Rui2; Fan Zhibin1; Ye Jie1; Wang Zhe2
2014
Source PublicationACTA METALLURGICA SINICA
ISSN0412-1961
Volume50Issue:5Pages:594-600
AbstractBy the investigation of the microstructures of Mg82.13Zn13.85Y4.02 (mass fraction, %) alloy solidified under different pressure, it is found that the solidification microstructure of the alloy is consisted of alpha-Mg matrix, W-Mg3Y2Zn3 phase and I-Mg3YZn6 phase. In the microstructure of the alloy solidified under ambient pressure, the networks of the secondary phases of eutectic-like and rod-like shape are distributed in the alpha-Mg interdendritic space. As the solidification pressure increases, eutectic network is disconnected gradually and the amount of eutectic is diminished and the solubility of Zn in alpha-Mg rises gradually. The results of the measurement of the mechanical properties show that the compression strength, the yield strength and the compressibility of the alloy sample solidified under ambient pressure is 344 MPa, 331 MPa and 16% respectively. However, the compression strength, the yield strength and the compressibility of the alloy sample solidified from 1250 degrees C under 6 GPa is 455 MPa, 426 MPa and 25%, respectively. The observation of fracture surfaces shows that, in the alloy solidified under high pressure, the cleavage surface of the compressed fracture is decreased, and the tear ridge and tearing dimple can be found. The degree of cleavage fracture is decreased.
KeywordZN-Y ALLOY MECHANICAL-PROPERTIES QUASI-CRYSTAL MORPHOLOGIES BEHAVIOR RATIO Mg82.13Zn13.85Y4.02 alloy high pressure solidification stress-strain curve cleavage surface
Indexed ByCSCD
Language英语
Funding Project[Natural Science Foundation of Hebei Province] ; [Natural Science Foundation of Liaoning Province] ; [Projiect of Science and Technology of Northeastern University at Qinhuangdao]
CSCD IDCSCD:5141014
Citation statistics
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/141562
Collection中国科学院金属研究所
Affiliation1.中国科学院金属研究所
2.Yanshan Univ, State Key Lab Metastable Materials Sci & Technol, Sch Materials Sci & Engn, Qinhuangdao 066004, Peoples R China
Recommended Citation
GB/T 7714
Dong Yun,Lin Xiaoping,Xu Rui,et al. MICROSTRUCTURE AND ROOM TEMPERATURE COMPRESSION PROPERTIES OF Mg82.13Zn13.85Y4.02 ALLOY SOLIDIFIED UNDER SUPER-HIGH PRESSURE[J]. ACTA METALLURGICA SINICA,2014,50(5):594-600.
APA Dong Yun,Lin Xiaoping,Xu Rui,Fan Zhibin,Ye Jie,&Wang Zhe.(2014).MICROSTRUCTURE AND ROOM TEMPERATURE COMPRESSION PROPERTIES OF Mg82.13Zn13.85Y4.02 ALLOY SOLIDIFIED UNDER SUPER-HIGH PRESSURE.ACTA METALLURGICA SINICA,50(5),594-600.
MLA Dong Yun,et al."MICROSTRUCTURE AND ROOM TEMPERATURE COMPRESSION PROPERTIES OF Mg82.13Zn13.85Y4.02 ALLOY SOLIDIFIED UNDER SUPER-HIGH PRESSURE".ACTA METALLURGICA SINICA 50.5(2014):594-600.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Dong Yun]'s Articles
[Lin Xiaoping]'s Articles
[Xu Rui]'s Articles
Baidu academic
Similar articles in Baidu academic
[Dong Yun]'s Articles
[Lin Xiaoping]'s Articles
[Xu Rui]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Dong Yun]'s Articles
[Lin Xiaoping]'s Articles
[Xu Rui]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.