Y、Gd、La和Ce对Zr(-Ti)-Cu-Ni-Al非晶形成能力和力学性能的影响

IMR OpenIR

	Y、Gd、La和Ce对Zr(-Ti)-Cu-Ni-Al非晶形成能力和力学性能的影响
其他题名	Effect of Y,Gd,La and Ce on the Glass Forming Ability and Mechanical Properties of Zr（-Ti）-Cu-Ni-Al Metallic Glasses
	李正坤 1; 秦鑫冬 1; 刘丁铭 1; 陆宏煜 1; 张海峰 1; 李扬德 2; 李卫荣 2
	2018
发表期刊	稀有金属材料与工程
ISSN	1002-185X
卷号	47.0 期号:009 页码:2755-2760
摘要	为了控制Zr(-Ti)-Cu-Ni-Al非晶合金中的O含量,进而改善其玻璃形成能力和力学性能,本研究基于稀土元素与O的强相互作用,向合金中添加Y、Gd、La和Ce等元素。使用铜模浇铸制备非晶合金,利用DSC、XRD和TEM对其非晶形成能力和微观结构进行分析,通过压缩试验和SEM对其力学性能及断裂方式进行表征。结果表明:Y的添加对合金的非晶形成能力具有较大的提升,在相对较低真空的气氛下,可制备出直径10mm以上的块体非晶,抗压缩断裂强度达1950 MPa。
其他摘要	Y,Gd,La and Ce were added into Zr（-Ti）-Cu-Ni-Al metallic glasses based on the mechanism of strong interaction between O and rare earth elements in order to control the O content and further to improve the glass forming ability and mechanical properties of the alloys.Metallic glasses were prepared by a copper mold casting method.The glass forming ability and microstructure of the alloys were studied by differential scanning calorimetry（DSC）,X-ray Diffraction（XRD） and transmission electron microscopy（TEM）,and the mechanical properties and corresponding fracture modes were investigated by quasi-static compressive tests and scanning electron microscope（SEM）.The results show that the addition of Y improves the glass forming ability greatly.Bulk metallic glasses with the diameter over 10 mm can be prepared under relatively low vacuum.The compressive strength is up to 1950 MPa.
关键词	非晶玻璃形成能力力学性能 Y
收录类别	CSCD
语种	中文
CSCD记录号	CSCD:6337276
引用统计	被引频次：4[CSCD] [CSCD记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/141623
专题	中国科学院金属研究所
作者单位	1.中国科学院金属研究所 2.东莞宜安科技股份有限公司
推荐引用方式 GB/T 7714	李正坤,秦鑫冬,刘丁铭,等. Y、Gd、La和Ce对Zr(-Ti)-Cu-Ni-Al非晶形成能力和力学性能的影响[J]. 稀有金属材料与工程,2018,47.0(009):2755-2760.
APA	李正坤.,秦鑫冬.,刘丁铭.,陆宏煜.,张海峰.,...&李卫荣.(2018).Y、Gd、La和Ce对Zr(-Ti)-Cu-Ni-Al非晶形成能力和力学性能的影响.稀有金属材料与工程,47.0(009),2755-2760.
MLA	李正坤,et al."Y、Gd、La和Ce对Zr(-Ti)-Cu-Ni-Al非晶形成能力和力学性能的影响".稀有金属材料与工程 47.0.009(2018):2755-2760.