模拟人体体液中镁合金的腐蚀行为研究

IMR OpenIR

	模拟人体体液中镁合金的腐蚀行为研究
其他题名	Corrosion Behavior of Mg-Zn-Y-Nd Alloy in Simulated Body Fluid
	郏义征 1; 赵明君 2; 程世婧 3; 王保杰 2; 王硕 4; 盛立远 5; 许道奎 4
	2019
发表期刊	中国腐蚀与防护学报
ISSN	1005-4537
卷号	39.0 期号:006 页码:463-468
摘要	研究了Mg-6Zn-1.2Y-0.8Nd合金样品在Hank’s溶液中经预浸泡处理前后的腐蚀行为。结果表明,表面的腐蚀产物对基体可以起到一定的防护作用。经4 h预浸泡处理后,合金表面形成的产物膜较为均匀,对基体的防护作用最佳,其腐蚀电流密度为1.98μA/cm^2。随着预浸泡时间的进一步延长,合金表面形成的腐蚀产物膜增厚,会发生自身开裂或与基体脱落,加剧了局部腐蚀,致使产物膜对基体的腐蚀防护作用明显下降。经48 h预浸泡处理后,合金的腐蚀电流密度增加至3.64μA/cm^2。
其他摘要	The corrosion behavior of Mg-6Zn-1.2Y-0.8Nd alloy before and after pre-soaking in Hank’s solution was comparatively studied. Results revealed that the surface corrosion products formed during pre-shoaking can protect the substrate from corrosion attack to a certain extent. After pre-soaking for 4 h, the product film formed on the surface was relatively uniform and had the best protective effect on the matrix. The corrosion current density was 1.98 μA/cm^2. As the pre-soaking time was further extended,the corrosion products film formed on sample surfaces became thicker, and tend to be cracked and detached from the substrate, correspondingly the localized corrosion was accelerated, resulting in the decrease in their protective effect. After pre-soaking for 48 h, the corrosion current density of the alloy increased to 3.64 μA/cm^2.
关键词	镁合金生物材料产物膜局部腐蚀浸泡
收录类别	CSCD
语种	中文
CSCD记录号	CSCD:6649112
引用统计	被引频次：4[CSCD] [CSCD记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/142033
专题	中国科学院金属研究所
作者单位	1.四川建筑职业技术学院 2.沈阳理工大学 3.中国科学院 4.中国科学院金属研究所 5.北京大学
推荐引用方式 GB/T 7714	郏义征,赵明君,程世婧,等. 模拟人体体液中镁合金的腐蚀行为研究[J]. 中国腐蚀与防护学报,2019,39.0(006):463-468.
APA	郏义征.,赵明君.,程世婧.,王保杰.,王硕.,...&许道奎.(2019).模拟人体体液中镁合金的腐蚀行为研究.中国腐蚀与防护学报,39.0(006),463-468.
MLA	郏义征,et al."模拟人体体液中镁合金的腐蚀行为研究".中国腐蚀与防护学报 39.0.006(2019):463-468.