| Effect of additive on corrosion resistance of NiFe(2)O(4) ceramics as inert anodes | |
| Alternative Title | Effect of additive on corrosion resistance of NiFe_2O_4 ceramics as inert anodes |
| Xi Jinhui1; Xie Yingjie2; Yao Guangchun2; Liu Yihan2 | |
| 2008 | |
| Source Publication | TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA
 |
| ISSN | 1003-6326 |
| Volume | 18Issue:2Pages:356-360 |
| Abstract | In order to improve the corrosion resistance of NiFe(2)O(4) ceramics as inert anode, additive V(2)O(5) was added to raw materials NiO and Fe(2)O(3). The inert anodes of nickel-ferrite ceramics were prepared by powder metallurgic method and the static corrosion rate in Na(3)AlF(6)-Al(2)O(3) was determined by mass loss measurement. The effect Of V(2)O(5) on sintering property and corrosion resistance was studied. The results show that V(2)O(5) can promote the grain to develop completely and improve sintering property. EDS results show the reaction product Ni(2)FeVO(6) distributes along the grain boundary. The corrosion tests show that V(2)O(5) is beneficial to improving corrosion resistance remarkably. The reasons that V(2)O(5) can improve the corrosion resistance must be V(2)O(5) promoting the gains to develop completely and Ni(2)FeVO(6) distributes along the grain boundary. The stable structure can control the chemical dissolution of ceramics anode and the reinforced grain boundary can control the grain-boundary corrosion rate. |
| Other Abstract | In order to improve the corrosion resistance of NiFe_2O_4 ceramics as inert anode, additive V_2O_5 was added to raw materials NiO and Fe_2O_3. The inert anodes of nickel-ferrite ceramics were prepared by powder metallurgic method and the static corrosion rate in Na_3AlF_6-Al_2O_3 was determined by mass loss measurement. The effect of V_2O_5 on sintering property and corrosion resistance was studied. The results show that V_2O_5 can promote the grain to develop completely and improve sintering property. EDS results show the reaction product Ni_2FeVO_6 distributes along the grain boundary. The corrosion tests show that V_2O_5 is beneficial to improving corrosion resistance remarkably. The reasons that V_2O_5 can improve the corrosion resistance must be V_2O_5 promoting the gains to develop completely and Ni_2FeVO_6 distributes along the grain boundary. The stable structure can control the chemical dissolution of ceramics anode and the reinforced grain boundary can control the grain-boundary corrosion rate. |
| Keyword | ALUMINUM ELECTROLYSIS CERMETS NiFe(2)O(4) inert anode additive corrosion resistance |
| Indexed By | CSCD |
| Language | 英语 |
| CSCD ID | CSCD:3252039 |
| Citation statistics |
Cited Times:7[CSCD]
[CSCD Record]
|
| Document Type | 期刊论文 |
| Identifier | http://ir.imr.ac.cn/handle/321006/142138 |
| Collection | 中国科学院金属研究所 |
| Affiliation | 1.中国矿业大学 2.中国科学院金属研究所 |
| Recommended Citation GB/T 7714 | Xi Jinhui,Xie Yingjie,Yao Guangchun,et al. Effect of additive on corrosion resistance of NiFe(2)O(4) ceramics as inert anodes[J]. TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA,2008,18(2):356-360. |
| APA | Xi Jinhui,Xie Yingjie,Yao Guangchun,&Liu Yihan.(2008).Effect of additive on corrosion resistance of NiFe(2)O(4) ceramics as inert anodes.TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA,18(2),356-360. |
| MLA | Xi Jinhui,et al."Effect of additive on corrosion resistance of NiFe(2)O(4) ceramics as inert anodes".TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA 18.2(2008):356-360. |
| Files in This Item: | There are no files associated with this item. | |||||
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment