Effect of Aging Heat Treatment on Microstructure and Properties of Laser Deposition Repaired GH738 Alloy
Bian Hongyou; Zhai Quanxing; Qu Shen; Yang Guang; Wang Wei; Wang Wei
2019
Source PublicationRARE METAL MATERIALS AND ENGINEERING
ISSN1002-185X
Volume48Issue:1Pages:317-322
AbstractThe effects of bipolar aging heat treatment on the microstructure and mechanical properties of GH738 alloy repaired by laser deposition were studied. The results show that the microstructure of repair area presents typical characteristics of the epitaxial growth of columnar crystals and the dendrite spacing is about 10 gm. After the aging treatment, the repair area begins to grow and merge. The results of SEM analysis show that there is no gamma' at the as-deposited sample, and the cubic MC type carbide is formed at the interdendritic, and the M23C6 type carbide at the dendrite arm. After the aging treatment, gamma' phase precipitates at the repair area whose average size is 37 nm, and the carbide precipitates in the grain boundary with the discontinued character when the temperature of the stabilization step is 820 degrees C. With the increase of the stabilization temperature, the size of the gamma' and carbide increases. When the temperature is 840 degrees C, the average size of the gamma' is about 76 nm, and the carbide is precipitated in the form of necklace. With increasing the temperature of the stabilization step to 860 degrees C, the average size of the gamma' does not increase obviously, and part of the gamma' is obviously coarsened and the size reaches to 150 nm; meanwhile the carbides at the grain boundaries begin to be closed. The results of mechanical property show that the tensile strength of the sample increases obviously after aging treatment, and with the increase of the temperature, the tensile strength increases first and then decreases, and the elongation decreases continuously.
KeywordPRECIPITATION SUPERALLOY laser deposition repair GH738 alloy heat treatment microstructure mechanical properties
Indexed ByCSCD
Language英语
CSCD IDCSCD:6412137
Citation statistics
Cited Times:2[CSCD]   [CSCD Record]
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/143201
Collection中国科学院金属研究所
Affiliation中国科学院金属研究所
Recommended Citation
GB/T 7714
Bian Hongyou,Zhai Quanxing,Qu Shen,et al. Effect of Aging Heat Treatment on Microstructure and Properties of Laser Deposition Repaired GH738 Alloy[J]. RARE METAL MATERIALS AND ENGINEERING,2019,48(1):317-322.
APA Bian Hongyou,Zhai Quanxing,Qu Shen,Yang Guang,Wang Wei,&Wang Wei.(2019).Effect of Aging Heat Treatment on Microstructure and Properties of Laser Deposition Repaired GH738 Alloy.RARE METAL MATERIALS AND ENGINEERING,48(1),317-322.
MLA Bian Hongyou,et al."Effect of Aging Heat Treatment on Microstructure and Properties of Laser Deposition Repaired GH738 Alloy".RARE METAL MATERIALS AND ENGINEERING 48.1(2019):317-322.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Bian Hongyou]'s Articles
[Zhai Quanxing]'s Articles
[Qu Shen]'s Articles
Baidu academic
Similar articles in Baidu academic
[Bian Hongyou]'s Articles
[Zhai Quanxing]'s Articles
[Qu Shen]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Bian Hongyou]'s Articles
[Zhai Quanxing]'s Articles
[Qu Shen]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.