| 大型锻件坯料内裂纹愈合的物理模拟 | |
| 其他题名 | Physical simulation of internal crack healing in a heavy-forged billet |
| 米国发1; 张军强1; 徐斌2; 孙明月2 | |
| 2017 | |
| 发表期刊 | 工程科学学报
 |
| ISSN | 2095-9389 |
| 卷号 | 39.0期号:011页码:1674-1683 |
| 摘要 | 针对锻造过程中钢锭内部裂纹缺陷的愈合情况进行研究,设计了裂纹愈合的实验室模拟实验与工业级模拟实验.通过在Gleeble热压缩试样中预制裂纹缺陷,研究了变形温度和变形量对内部裂纹愈合的影响,发现变形温度越高,变形量越大,内裂纹的愈合效果越好.为了验证Gleeble实验结果的准确性,保证其结果在实际锻造生产中的适用性,设计了锻件内部裂纹愈合的工业级模拟实验.结果表明在1200℃,变形量为40%时,可以有效焊合锻件内部裂纹. |
| 其他摘要 | The healing behavior of internal cracks in an ingot during the forging process was investigated using laboratory and industrial simulation studies. During the laboratory experiment,specimens with artificial cracks were hot compressed by a Gleeble simulator,and the effect of temperature and deformation ratio on inner crack healing was studied. The experimental result shows that the higher the deformation temperature or greater the deformation,the better the healing effect. To verify the accuracy and applicability of the result in an actual forging process,an industrial experiment was designed and performed. The result shows that internal cracks can be effectively metallurgically bonded at a temperature of 1200 ℃ and deformation ratio of 40%. |
| 关键词 | 大型锻件 内裂纹 愈合 变形 变形温度 |
| 收录类别 | CSCD |
| 语种 | 中文 |
| CSCD记录号 | CSCD:6126073 |
| 引用统计 | |
| 文献类型 | 期刊论文 |
| 条目标识符 | http://ir.imr.ac.cn/handle/321006/145221 |
| 专题 | 中国科学院金属研究所 |
| 作者单位 | 1.河南理工大学 2.中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | 米国发,张军强,徐斌,等. 大型锻件坯料内裂纹愈合的物理模拟[J]. 工程科学学报,2017,39.0(011):1674-1683. |
| APA | 米国发,张军强,徐斌,&孙明月.(2017).大型锻件坯料内裂纹愈合的物理模拟.工程科学学报,39.0(011),1674-1683. |
| MLA | 米国发,et al."大型锻件坯料内裂纹愈合的物理模拟".工程科学学报 39.0.011(2017):1674-1683. |
| 条目包含的文件 | 条目无相关文件。 | |||||
| 个性服务 |
| 推荐该条目 |
| 保存到收藏夹 |
| 查看访问统计 |
| 导出为Endnote文件 |
| 谷歌学术 |
| 谷歌学术中相似的文章 |
| [米国发]的文章 |
| [张军强]的文章 |
| [徐斌]的文章 |
| 百度学术 |
| 百度学术中相似的文章 |
| [米国发]的文章 |
| [张军强]的文章 |
| [徐斌]的文章 |
| 必应学术 |
| 必应学术中相似的文章 |
| [米国发]的文章 |
| [张军强]的文章 |
| [徐斌]的文章 |
| 相关权益政策 |
| 暂无数据 |
| 收藏/分享 |
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论