电弧离子镀梯度(Ti,Al)N薄膜的结构与抗氧化性能
Alternative TitleSTRUCTURE AND OXIDATION BEHAVIOR OF GRADIENT (Ti, Al)N FILM PREPARED BY ARC ION PLATING
冯长杰; 辛丽; 李明升; 朱圣龙; 王福会
2008
Source Publication中国腐蚀与防护学报
ISSN1005-4537
Volume28.0Issue:1.0Pages:1-6
Abstract采用电弧离子镀(AIP)技术在航空发动机压气机用1Cr11Ni2W2MoV不锈钢上沉积(Ti,Al)N梯度薄膜,并研究其微观结构和高温抗氧化性能。结果表明,薄膜均匀致密,与基体结合良好;薄膜为B1型(NaCl)单相结构,具有(220)择优取向;薄膜是内层富TiN、外层富(Ti,Al)N的梯度薄膜;梯度薄膜在700℃和800oC氧化后,表层形成富Al2O3的保护膜,在700℃较长时间内和800℃短时间内对不锈钢基体具有良好的保护作用。
Other AbstractGradient (Ti,Al)N film was deposited on 1Crl 1Ni2W2MoV stainless steel for aero-engine compressor blades by arc ion plating. The microstructure of the film and the high temperature oxidation behavior of the coated steel were studied results showed that the gradient film had a B1 (NaCl) structure with (220) preferred orientation, and with inner layer rich in TiN and outer layer rich in (Ti ,Al)N. The film was very dense and adhensiwe.The oxidation results indicated that the gradient films were protective at 700 ℃ for long time and at 800 ℃ for short time. It was found that protective layers rich in amorphous alumina formed on top of the gradient (Ti,Al)N film during the elevated temperature oxidation which protected the film from further oxidation
Keyword电弧离子镀 梯度(Ti Al)N薄膜 结构 氧化
Indexed ByCSCD
Language中文
CSCD IDCSCD:3247669
Citation statistics
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/145641
Collection中国科学院金属研究所
Affiliation中国科学院金属研究所
Recommended Citation
GB/T 7714
冯长杰,辛丽,李明升,等. 电弧离子镀梯度(Ti,Al)N薄膜的结构与抗氧化性能[J]. 中国腐蚀与防护学报,2008,28.0(1.0):1-6.
APA 冯长杰,辛丽,李明升,朱圣龙,&王福会.(2008).电弧离子镀梯度(Ti,Al)N薄膜的结构与抗氧化性能.中国腐蚀与防护学报,28.0(1.0),1-6.
MLA 冯长杰,et al."电弧离子镀梯度(Ti,Al)N薄膜的结构与抗氧化性能".中国腐蚀与防护学报 28.0.1.0(2008):1-6.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[冯长杰]'s Articles
[辛丽]'s Articles
[李明升]'s Articles
Baidu academic
Similar articles in Baidu academic
[冯长杰]'s Articles
[辛丽]'s Articles
[李明升]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[冯长杰]'s Articles
[辛丽]'s Articles
[李明升]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.