镁合金应力腐蚀开裂行为研究进展
Alternative TitleResearch Progress on Stress Corrosion Cracking Behavior of Magnesium Alloys
王保杰1; 栾吉瑜1; 王士栋2; 许道奎2
2019
Source Publication中国腐蚀与防护学报
ISSN1005-4537
Volume000Issue:002Pages:89-95
Abstract系统总结了镁合金的应力腐蚀开裂行为及其微观失效机制的研究进展,重点介绍了阳极溶解、机械载荷、氢脆效应等对裂纹开裂模式的影响和作用规律,以及提高镁合金抗应力腐蚀开裂能力的处理方法及其作用机制;指出目前研究中存在的问题,并提出未来的研究重点和发展方向。
Other AbstractIn this paper,the stress corrosion cracking(SCC)behavior of Mg-alloys and the relevant failure mechanism were systematically summarized.Moreover,the effect of anodic dissolution,mechanical loading and hydrogen embrittlement on the SCC cracking modes was described.The measures for improving the SCC resistance of Mg-alloys were also introduced.Finally,the existing problems in the current study,the research emphasis and direction in the future are also pointed out.
Keyword镁合金 应力腐蚀开裂 局部腐蚀 氢致开裂 腐蚀机制
Indexed ByCSCD
Language中文
CSCD IDCSCD:6491509
Citation statistics
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/147782
Collection中国科学院金属研究所
Affiliation1.沈阳理工大学
2.中国科学院金属研究所
Recommended Citation
GB/T 7714
王保杰,栾吉瑜,王士栋,等. 镁合金应力腐蚀开裂行为研究进展[J]. 中国腐蚀与防护学报,2019,000(002):89-95.
APA 王保杰,栾吉瑜,王士栋,&许道奎.(2019).镁合金应力腐蚀开裂行为研究进展.中国腐蚀与防护学报,000(002),89-95.
MLA 王保杰,et al."镁合金应力腐蚀开裂行为研究进展".中国腐蚀与防护学报 000.002(2019):89-95.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[王保杰]'s Articles
[栾吉瑜]'s Articles
[王士栋]'s Articles
Baidu academic
Similar articles in Baidu academic
[王保杰]'s Articles
[栾吉瑜]'s Articles
[王士栋]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[王保杰]'s Articles
[栾吉瑜]'s Articles
[王士栋]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.