涂覆Ni—Cr—Al—Y涂层的镍基高温合金热机械疲劳行为
Alternative TitleTHERMO-MECHANICAL FATIGUE BEHAVIOR OF Ni- BASED SUPERALLOY COATED WITH Ni-Cr-Al-Y
陈竹兵; 黄志伟; 王中光; 朱世杰
2009
Source Publication金属学报
ISSN0412-1961
Volume45.0Issue:007Pages:820-825
Abstract分别采取大气等离子(APS)和高速火焰(HVOF)工艺制备Ni—Cr-Al-Y涂层.对涂覆Ni—Cr-Al—Y涂层的高温合金试样的热机械疲劳(TMF)行为进行了研究.结果表明:在相同应变幅下,2种涂层试样都是反相位热机械疲劳(OPTMF)寿命比同相位热机械疲劳(IPTMF)寿命短;在不同应变幅下,试样的热机械疲劳寿命与涂层的喷涂工艺相关.通过断口和纵向剖面图的观察分析表明,裂纹的萌生对试样的寿命有很大的影响.
Other AbstractGas turbine engine is widely used in industry, marine and aerospace. Its efficiency can be enhanced by increasing inlet gas temperature and reducing heat transfer. To achieve this goal it is important to develop materials with higher melting points. Ni based superalloy is suitable for vane and blade materials. The properties of superalloy have been improved by directionally solidified and single crystal in last 50 years. But it is limited to develop superalloy with much higher temperature, because the operating temperature approaches the melting point of superalloy. In this rigorous environment, high temperature oxidation and hot corrosion impair the alloy property. MCrAlY coating is commonly used as oxidation- and corrosion resistant material. Hitherto, it is clearly validated that the oxidation- and corrosion-resistance of hot parts at high temperature can be greatly improved by MCrAlY coating. The difference of materials properties between MCrAlY coating and superalloy may cause interactions which influence the mechanical properties and life of MCrAlY-coated component. A few of studies have conducted on mechanical properties of MCrAlY-coated superalloy. The results revealed that the present of coating affected the performance of superalloy. In service, thermo-mechanical fatigue provides a closer simulation of the actual strain-temperature in an engine environment. Only a few studies were published though their results were not consistency; because the experiment is hard to perform and many factors influence the experiment results such as temperature-strain cycle shape, strain range magnitude, the ductility and the strength of the bond between the coating and the substrate.In this paper, thermo-mechanical fatigue (TMF) behaviors of a Ni-based superalloy M963 coated with Ni-Cr-Al-Y have been investigated at 450--900 ℃in air under mechanical strain control with a strain ratio of -1 and a period of 200 s. The coating was produced either by air plasma spraying (APS) or by high velocity oxyfuel fuel (HVOF). It was shown that under the same mechanical strain, the out of phase (OP) TMF life is shorter than the in phase (IP) TMF one in both APS and HVOF coated specimens. The TMF life depends on the coating spraying technology under the same testing conditions. Observations of fracture surfaces and longitudinal sections revealed that crack initiation has great impact on the TMF life.
Keyword镍基高温合金 Ni—Cr—Al—Y 涂层 热机械疲劳 裂纹萌生与扩展
Indexed ByCSCD
Language中文
CSCD IDCSCD:3664574
Citation statistics
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/153098
Collection中国科学院金属研究所
Affiliation中国科学院金属研究所
Recommended Citation
GB/T 7714
陈竹兵,黄志伟,王中光,等. 涂覆Ni—Cr—Al—Y涂层的镍基高温合金热机械疲劳行为[J]. 金属学报,2009,45.0(007):820-825.
APA 陈竹兵,黄志伟,王中光,&朱世杰.(2009).涂覆Ni—Cr—Al—Y涂层的镍基高温合金热机械疲劳行为.金属学报,45.0(007),820-825.
MLA 陈竹兵,et al."涂覆Ni—Cr—Al—Y涂层的镍基高温合金热机械疲劳行为".金属学报 45.0.007(2009):820-825.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[陈竹兵]'s Articles
[黄志伟]'s Articles
[王中光]'s Articles
Baidu academic
Similar articles in Baidu academic
[陈竹兵]'s Articles
[黄志伟]'s Articles
[王中光]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[陈竹兵]'s Articles
[黄志伟]'s Articles
[王中光]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.