乙醇/水混合溶剂热法制备BaHfO3:Ce超微粒子 | |
Alternative Title | Preparation of BaHfO3:Ce Ultra-fine Particles by C2H5OH/H2O Mixed Solvolthermal Method |
苑晓宇; 马伟民; 闻雷; 杨化仁 | |
2011 | |
Source Publication | 人工晶体学报
![]() |
ISSN | 1000-985X |
Volume | 40.0Issue:002Pages:486-491 |
Abstract | 以Ba(NO3)2和HfOCl2.8H2O为原料,KOH为矿化剂,乙醇/水作溶剂,Ce(NO3)3作为激活剂,在150-220℃和16-36 h的条件下,制备了掺杂Ce^3+的BaHfO3超微粒子。用XRD,SEM等手段表征了粒子合成过程的物相变化及形貌特征;用荧光光度计分析了样品的激发光谱和发射光谱。结果表明,在n(Ba)∶n(Hf)=1∶1,水热合成温度200℃,保温时间24 h,pH=13.5的条件下制备的BaHfO3∶Ce粒子分散性好,形貌近球形,粒径约52 nm。当掺杂Ce3+浓度为0.3 mol%时BaHfO3发光效果最佳。 |
Other Abstract | The BaHfO3∶Ce ultra-fine particles were prepared by C2H5OH/H2O mixed solvolthermal method,under 150-220 ℃ for 16-36 h using Ba(NO3)2 and HfOCl2·8H2O as raw materials,added KOH aqueous solution as precipitant and Ce(NO3)3 aqueous solution as activator.The phase transformation and the morphology of powders during preparation of BaHfO3∶Ce powders were studied by XRD and SEM.The excitation and emission spectra of samples were analyzed by the fluor-photometer.The results show that the powders are approximately spherical particles with even particle size of about 52 nm and good dispersibility under the condition of n(Ba)∶n(Hf)=1∶1,pH=13.5,treated at 200 ℃ for 24 h.The superior photoluminescence properties were obtained at dopping of 0.3 mol % Ce. |
Keyword | BaHfO3:Ce粒子 水热法 物相变化 光谱特性 |
Indexed By | CSCD |
Language | 中文 |
CSCD ID | CSCD:4179443 |
Citation statistics |
Cited Times:2[CSCD]
[CSCD Record]
|
Document Type | 期刊论文 |
Identifier | http://ir.imr.ac.cn/handle/321006/153617 |
Collection | 中国科学院金属研究所 |
Affiliation | 中国科学院金属研究所 |
Recommended Citation GB/T 7714 | 苑晓宇,马伟民,闻雷,等. 乙醇/水混合溶剂热法制备BaHfO3:Ce超微粒子[J]. 人工晶体学报,2011,40.0(002):486-491. |
APA | 苑晓宇,马伟民,闻雷,&杨化仁.(2011).乙醇/水混合溶剂热法制备BaHfO3:Ce超微粒子.人工晶体学报,40.0(002),486-491. |
MLA | 苑晓宇,et al."乙醇/水混合溶剂热法制备BaHfO3:Ce超微粒子".人工晶体学报 40.0.002(2011):486-491. |
Files in This Item: | There are no files associated with this item. |
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment