熔体处理对一种Inconel718C改型高温合金组织与性能的影响
Alternative TitleEffect of Melt Treatment on Microstructure and Property of a Modified Inconel 718C Alloy
陈伟; 李长春; 李辉; 楼琅洪; 陈光
2007
Source Publication铸造
ISSN1001-4977
Volume56.0Issue:003Pages:248-250
Abstract在试验合金中,1600℃熔体处理对凝固后组织和性能产生显著影响。经1600℃熔体处理后,合金样品二次枝晶间距显著降低,元素偏析情况得到有效改善,凝固过程析出的TCP相数量明显减少,热处理后℃析出相也更加细小均匀。熔体处理对合金室温和700℃拉伸强度影响不大,但却显著提高合金的拉伸塑性和700/620MPa持久性能。在1600℃熔体处理10min时,合金的综合力学性能最佳;延长熔体处理时间至15min时,合金力学性能呈下降趋势。
Other AbstractEffect of melt treatment on the microstructure and mechanical properties of a modified inconel 718C alloy was studied in this paper. The results show that, microstructure of finer dendrite, lower segregation and less amount of Laves phase is obtained after melt treatment. Also, smaller γ'' phases with more uniform distribution are precipitating in the specimen via melt treatment. Melt treatment shows no obvious effect on the 25℃ and 700℃ tensile strength, while it evidently improves the tensile plasticity and the stress-rupture property. Specimens via melt treatment at 1 600 ℃ for 10 minutes exhibit best mechanical properties. Extended melt treatment after 10 minutes degrades the mechanical properties.
Keyword高温合金 熔体处理 偏析 力学性能
Indexed ByCSCD
Language中文
CSCD IDCSCD:2719597
Citation statistics
Cited Times:4[CSCD]   [CSCD Record]
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/154936
Collection中国科学院金属研究所
Affiliation中国科学院金属研究所
Recommended Citation
GB/T 7714
陈伟,李长春,李辉,等. 熔体处理对一种Inconel718C改型高温合金组织与性能的影响[J]. 铸造,2007,56.0(003):248-250.
APA 陈伟,李长春,李辉,楼琅洪,&陈光.(2007).熔体处理对一种Inconel718C改型高温合金组织与性能的影响.铸造,56.0(003),248-250.
MLA 陈伟,et al."熔体处理对一种Inconel718C改型高温合金组织与性能的影响".铸造 56.0.003(2007):248-250.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[陈伟]'s Articles
[李长春]'s Articles
[李辉]'s Articles
Baidu academic
Similar articles in Baidu academic
[陈伟]'s Articles
[李长春]'s Articles
[李辉]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[陈伟]'s Articles
[李长春]'s Articles
[李辉]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.