Impacts of aging treatments on the microstructural evolutions, mechanical properties and strengthening mechanism in 1Cr15Ni36W3Ti
Li, Haoze; Zhang, Weina; Li, Min; Gao, Ming; Ma, Yingche; Liu, Kui
2020-12-20
Source PublicationJOURNAL OF ALLOYS AND COMPOUNDS
Volume847
AbstractThe microstructural evolution, mechanical properties, fracture behaviors and age hardening mechanism in 1Cr15Ni36W3Ti subjected to various thermal treatments involving a preceding solution at 1080 degrees C and three distinct aging schedules were investigated. Upon aging treated at 870 degrees C and then 700 degrees C, discrete globular MC carbides combined with dispersive and fine gamma' particles were formed at grain boundaries and in the gamma matrix, respectively, which is beneficial in resisting the propagation of grain-boundary microcracks and dramatically enhancing yield and ultimate strengths. Rather, the second aging strategy conducted at 730 degrees C after solution resulted in relatively coarse gamma' precipitates and nearly continuous intergranular MC carbides, while the third aging schedule carried out firstly at 780 degrees C and then 730 degrees C led to a dual size of gamma' phase and also a nearly continuous distribution of the grain-boundary MC carbides. Moreover, gamma' denuded zones on both sides of grain boundaries were formed in the latter two aging treatments, which were severer in the third age. The relatively coarse gamma' phase and the appearance of precipitate-free zones dramatically lowered the strength, whereas the nearly continuous intergranular carbides with gamma' denuded zones alongside accelerated the propagation of intergranular micro-cracks. Dislocation shearing was dominated. The gamma' coherency strengthening, the introduction of complex stacking faults in the gamma' phase arising from Shockley partial dislocations shearing and the elimination of gamma' denuded zones were responsible for the highest tensile strength when undergoing the first-type age. (C) 2020 Elsevier B.V. All rights reserved.
DOI10.1016/j.jallcom.2020.156510
WOS IDWOS:000573225900010
Citation statistics
Cited Times:1[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/155640
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
Li, Haoze,Zhang, Weina,Li, Min,et al. Impacts of aging treatments on the microstructural evolutions, mechanical properties and strengthening mechanism in 1Cr15Ni36W3Ti[J]. JOURNAL OF ALLOYS AND COMPOUNDS,2020,847.
APA Li, Haoze,Zhang, Weina,Li, Min,Gao, Ming,Ma, Yingche,&Liu, Kui.(2020).Impacts of aging treatments on the microstructural evolutions, mechanical properties and strengthening mechanism in 1Cr15Ni36W3Ti.JOURNAL OF ALLOYS AND COMPOUNDS,847.
MLA Li, Haoze,et al."Impacts of aging treatments on the microstructural evolutions, mechanical properties and strengthening mechanism in 1Cr15Ni36W3Ti".JOURNAL OF ALLOYS AND COMPOUNDS 847(2020).
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Li, Haoze]'s Articles
[Zhang, Weina]'s Articles
[Li, Min]'s Articles
Baidu academic
Similar articles in Baidu academic
[Li, Haoze]'s Articles
[Zhang, Weina]'s Articles
[Li, Min]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Li, Haoze]'s Articles
[Zhang, Weina]'s Articles
[Li, Min]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.