Thermal shock and sulfuric acid corrosion behavior of enamel-nano-Ni composite/enamel-nano-nickel composite coating

doi:10.1111/ijag.15513

IMR OpenIR

	Thermal shock and sulfuric acid corrosion behavior of enamel-nano-Ni composite/enamel-nano-nickel composite coating
	Chen, Ken; Chen, Minghui; Yi, Aihua; Li, Kang; Zhu, Wen; Liao, Zhongmiao; Zhu, Shenglong; Wang, Fuhui
	2020-10-01
发表期刊	INTERNATIONAL JOURNAL OF APPLIED GLASS SCIENCE
卷号	11 期号:4 页码:784-795
摘要	Dense and well-adherent enamel-nano-Ni composite/enamel-nano-nickel composite coatings were prepared on 304 steel. Their thermal shock (TS) resistance at 400 degrees C as well as the chemical stability in sulfuric acid solution were investigated, and compared with pure enamel coatings. Results indicated that the nanocomposite coatings with 5 wt% of Ni particles exhibited the best resistance to TS. Almost no spalling of the coating occurs after 50 cycles of TS at 400 degrees C. They also provided enough protective effect to the substrates from sulfuric acid corrosion. After 7 days of corrosion, the weight loss of Ni-5 enamel coating was only 1.107 mg/cm(.)(2)
DOI	10.1111/ijag.15513
WOS记录号	WOS:000530521500001
引用统计	被引频次：6[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/155702
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	Chen, Ken,Chen, Minghui,Yi, Aihua,et al. Thermal shock and sulfuric acid corrosion behavior of enamel-nano-Ni composite/enamel-nano-nickel composite coating[J]. INTERNATIONAL JOURNAL OF APPLIED GLASS SCIENCE,2020,11(4):784-795.
APA	Chen, Ken.,Chen, Minghui.,Yi, Aihua.,Li, Kang.,Zhu, Wen.,...&Wang, Fuhui.(2020).Thermal shock and sulfuric acid corrosion behavior of enamel-nano-Ni composite/enamel-nano-nickel composite coating.INTERNATIONAL JOURNAL OF APPLIED GLASS SCIENCE,11(4),784-795.
MLA	Chen, Ken,et al."Thermal shock and sulfuric acid corrosion behavior of enamel-nano-Ni composite/enamel-nano-nickel composite coating".INTERNATIONAL JOURNAL OF APPLIED GLASS SCIENCE 11.4(2020):784-795.