Precipitation Behavior and Mechanical Properties of a 16Cr-25Ni Superaustenitic Stainless Steel Weld Metal During Post-weld Heat Treatment
Tian, Wenbin1,2; Wu, Dong1; Li, Yiyi1,3; Lu, Shanping1
通讯作者Lu, Shanping(shplu@imr.ac.cn)
2021-07-08
发表期刊ACTA METALLURGICA SINICA-ENGLISH LETTERS
ISSN1006-7191
页码14
摘要A 16Cr-25Ni superaustenitic stainless steel weld metal for austenitic stainless steel/ferrite heat-resistance steel dissimilar metal weld was designed and prepared through tungsten inert-gas welding. The precipitate evolution and its correlation with mechanical properties were investigated during post-weld heat treatment (PWHT) at 690 degrees C for up to 12 h. The primary precipitates in the as-welded weld metal were identified as Mo-rich M6C carbides in the interdendritic region and semicontinuous fine-sized M23C6 carbides along grain boundary. After PWHT, three types of precipitates coexisted in the interdendritic region: primary M6C carbides, newly precipitated Mo-rich M2X carbonitrides and some of the secondary M23C6 carbides. Additionally, mass secondary M23C6 carbides formed and coarsened along grain boundary. No undesirable intermetallic phases formed during the whole period. The M2X and interdendritic M23C6 improved the strength of the weld metal after PWHT, but the elongation and impact toughness degraded, which were mainly owing to the intergranular M23C6 carbides that changed the fracture mode from ductile transgranular mode to mixed mode of transgranular and intergranular fracture. Meanwhile, the coarsening of M2X carbonitrides may lead to the elongation loss during 8 h to 12 h. Evolution of impact toughness was also related to the M2X carbonitrides, which made the crack easier to propagate compared with austenitic matrix and contributed to the decline of impact toughness. However, due to the sluggish precipitation of M2X carbonitrides with longer holding time, the decreasing trend became slow from 4 to 12 h. The results showed that PWHT should be controlled within 8 h to obtain better combination of strength and ductility.
关键词Superaustenitic stainless steel Weld metal Post-weld heat treatment Precipitate evolution Mechanical properties
资助者innovation project of Shenyang National Laboratory for Materials Science
DOI10.1007/s40195-021-01274-6
收录类别SCI
语种英语
资助项目innovation project of Shenyang National Laboratory for Materials Science[SYNL-2019]
WOS研究方向Metallurgy & Metallurgical Engineering
WOS类目Metallurgy & Metallurgical Engineering
WOS记录号WOS:000670867100001
出版者CHINESE ACAD SCIENCES, INST METAL RESEARCH
引用统计
被引频次:10[WOS]   [WOS记录]     [WOS相关记录]
文献类型期刊论文
条目标识符http://ir.imr.ac.cn/handle/321006/160157
专题中国科学院金属研究所
通讯作者Lu, Shanping
作者单位1.Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Peoples R China
2.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China
3.Chinese Acad Sci, Inst Met Res, CAS Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Peoples R China
推荐引用方式
GB/T 7714
Tian, Wenbin,Wu, Dong,Li, Yiyi,et al. Precipitation Behavior and Mechanical Properties of a 16Cr-25Ni Superaustenitic Stainless Steel Weld Metal During Post-weld Heat Treatment[J]. ACTA METALLURGICA SINICA-ENGLISH LETTERS,2021:14.
APA Tian, Wenbin,Wu, Dong,Li, Yiyi,&Lu, Shanping.(2021).Precipitation Behavior and Mechanical Properties of a 16Cr-25Ni Superaustenitic Stainless Steel Weld Metal During Post-weld Heat Treatment.ACTA METALLURGICA SINICA-ENGLISH LETTERS,14.
MLA Tian, Wenbin,et al."Precipitation Behavior and Mechanical Properties of a 16Cr-25Ni Superaustenitic Stainless Steel Weld Metal During Post-weld Heat Treatment".ACTA METALLURGICA SINICA-ENGLISH LETTERS (2021):14.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Tian, Wenbin]的文章
[Wu, Dong]的文章
[Li, Yiyi]的文章
百度学术
百度学术中相似的文章
[Tian, Wenbin]的文章
[Wu, Dong]的文章
[Li, Yiyi]的文章
必应学术
必应学术中相似的文章
[Tian, Wenbin]的文章
[Wu, Dong]的文章
[Li, Yiyi]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。