| Tensile Deformation and Fracture Behavior of Nickel-Based Superalloy DZ951G | |
| Guo, Chenhao1,2; Yu, Jinjiang1; Liu, Jinlai1; Sun, Xiaofeng1; Zhou, Yizhou1 | |
| 通讯作者 | Yu, Jinjiang(jjyu@imr.ac.cn) |
| 2021-05-01 | |
| 发表期刊 | MATERIALS
 |
| 卷号 | 14期号:9页码:11 |
| 摘要 | DZ951G is a novel developed nickel-based directional solidified superalloy with an incipient high melting point and low density. Compared with DZ417G superalloy, DZ951G superalloy has a higher ultimate tensile strength. At intermediate temperatures, the plasticity and strength were both markedly improved, and an obviously anomalous yield behavior could be observed where the yield strength reached its maximum at 760 degrees C. Below 600 degrees C, two competitive modes of dislocations shearing gamma ' particles existed, in which one was the formation of stacking faults and another was a/2 dislocations shearing. At intermediate temperatures, a transitional phase between shearing gamma ' particles and bypassing appeared, and the fracture translated from brittle fracture into ductile fracture. Exceeding 900 degrees C, bypassing of dislocations was operated under thermal activation. Moreover, short continuous stacking faults still existed at 760 degrees C. Finally, the various dislocation configurations were rationally illuminated and explained with the intrinsic connection of mechanical properties. |
| 关键词 | DZ951G superalloy tensile properties stacking faults microstructures deformation mechanisms |
| 资助者 | National Natural Science Foundation of China (NSFC) |
| DOI | 10.3390/ma14092250 |
| 收录类别 | SCI |
| 语种 | 英语 |
| 资助项目 | National Natural Science Foundation of China (NSFC)[51771191] ; National Natural Science Foundation of China (NSFC)[51971214] |
| WOS研究方向 | Chemistry ; Materials Science ; Metallurgy & Metallurgical Engineering ; Physics |
| WOS类目 | Chemistry, Physical ; Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering ; Physics, Applied ; Physics, Condensed Matter |
| WOS记录号 | WOS:000650555100001 |
| 出版者 | MDPI |
| 引用统计 | |
| 文献类型 | 期刊论文 |
| 条目标识符 | http://ir.imr.ac.cn/handle/321006/161526 |
| 专题 | 中国科学院金属研究所 |
| 通讯作者 | Yu, Jinjiang |
| 作者单位 | 1.Chinese Acad Sci, Shi Changxu Innovat Ctr Adv Mat, Inst Met Res, Shenyang 110016, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Guo, Chenhao,Yu, Jinjiang,Liu, Jinlai,et al. Tensile Deformation and Fracture Behavior of Nickel-Based Superalloy DZ951G[J]. MATERIALS,2021,14(9):11. |
| APA | Guo, Chenhao,Yu, Jinjiang,Liu, Jinlai,Sun, Xiaofeng,&Zhou, Yizhou.(2021).Tensile Deformation and Fracture Behavior of Nickel-Based Superalloy DZ951G.MATERIALS,14(9),11. |
| MLA | Guo, Chenhao,et al."Tensile Deformation and Fracture Behavior of Nickel-Based Superalloy DZ951G".MATERIALS 14.9(2021):11. |
| 条目包含的文件 | 条目无相关文件。 | |||||
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论