Effect of Minor Sc Addition on Microstructure and Tensile Properties of Hot-Extruded 7055 Alloy
Zhang, Guowei1; Feng, Xiaohui2; Yang, Yuansheng2
Corresponding AuthorZhang, Guowei(20030358@nuc.edu.cn) ; Feng, Xiaohui(xhfeng@imr.ac.cn)
2022-06-06
Source PublicationJOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE
ISSN1059-9495
Pages8
AbstractThe microstructure and tensile properties of hot-extruded Al-8Zn-2Mg-2Cu-0.15Zr alloy (7055 alloy) with the minor addition of Sc were investigated. The 0.1 and 0.2 wt.% Sc were added into 7055 alloy during the preparation process by conventional casting. Attributing to the Sc additions, the grain sizes of as-cast ingots were remarkably refined and the irregular grain morphology changed to nearly spherical. Correspondingly, the distinctly refined microstructure of the 7055 alloy with Sc addition was achieved after hot extrusion. Unlike most reported extrusion cases of 7055 alloy, the extrusion temperature and ram speed were set to be 500 degrees C and 0.1 mm/s, respectively. As the added Sc increased from 0 to 0.1 and 0.2 wt.%, the yield strength (YS) of the T6 treated samples of extruded 7055 alloys were improved from 652 to 660 and 695 MPa, and the ultimate tensile strength (UTS) was 701, 706, and 744 MPa, respectively. The elongation of all the T6 samples remained to be about 11.5%. The good tensile properties of these experimental alloys are mainly attributed to grain refinement, extrusion texture, and the abundant precipitated particles, including Al-3(ScZr) and eta(MgZn2), which effectively pin the dislocation and hinder the migration of grain boundaries.
KeywordAl alloy hot extrusion microstructure scandium addition tensile properties
Funding OrganizationNational Key Research and Development Program of China ; National Science and Technology Major Project ; Key Research and Development Plan of Shandong Province
DOI10.1007/s11665-021-06383-y
Indexed BySCI
Language英语
Funding ProjectNational Key Research and Development Program of China[2018YFE115800] ; National Science and Technology Major Project[2017-VI-0003-0073] ; Key Research and Development Plan of Shandong Province[2019JZZY020329]
WOS Research AreaMaterials Science
WOS SubjectMaterials Science, Multidisciplinary
WOS IDWOS:000806671200002
PublisherSPRINGER
Citation statistics
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/174192
Collection中国科学院金属研究所
Corresponding AuthorZhang, Guowei; Feng, Xiaohui
Affiliation1.North Univ China, Sch Mat Sci & Engn, Taiyuan 030051, Peoples R China
2.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China
Recommended Citation
GB/T 7714
Zhang, Guowei,Feng, Xiaohui,Yang, Yuansheng. Effect of Minor Sc Addition on Microstructure and Tensile Properties of Hot-Extruded 7055 Alloy[J]. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE,2022:8.
APA Zhang, Guowei,Feng, Xiaohui,&Yang, Yuansheng.(2022).Effect of Minor Sc Addition on Microstructure and Tensile Properties of Hot-Extruded 7055 Alloy.JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE,8.
MLA Zhang, Guowei,et al."Effect of Minor Sc Addition on Microstructure and Tensile Properties of Hot-Extruded 7055 Alloy".JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE (2022):8.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Zhang, Guowei]'s Articles
[Feng, Xiaohui]'s Articles
[Yang, Yuansheng]'s Articles
Baidu academic
Similar articles in Baidu academic
[Zhang, Guowei]'s Articles
[Feng, Xiaohui]'s Articles
[Yang, Yuansheng]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Zhang, Guowei]'s Articles
[Feng, Xiaohui]'s Articles
[Yang, Yuansheng]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.