Effects of Brazing Temperature on Microstructure and High-Temperature Strength of Joints Using a Novel Fourth-Generation Nickel-Based Single Crystal Superalloy
Zhang, Z. P.1,2; Liu, J. D.2; Qiu, K. Q.1; Huang, Y. Y.2; Li, J. G.2; Wang, X. G.2; Liu, J. L.2; Wang, M.2; Zou, M. K.2; Zhou, Y. Z.2
Corresponding AuthorLiu, J. D.(jdliu@imr.ac.cn) ; Qiu, K. Q.(kqqiu@sut.edu.cn)
2022-06-03
Source PublicationMETALS AND MATERIALS INTERNATIONAL
ISSN1598-9623
Pages13
AbstractA novel fourth-generation nickel-based single crystal superalloy was bonded by vacuum brazing at 1230 degrees C, 1260 degrees C and 1290 degrees C for 60 min using a new type of Co-based filler alloy. The effects of the brazing temperature on the microstructure and mechanical properties of the brazed joint were investigated. The brazed joint was mainly composed of the non-isothermal solidification zone (M3B2 type-boride, CrB boride, Ni3B boride and MC carbide), isothermal solidification zone (gamma and gamma' Phase) and base metal. With the increase of brazing temperature, the volume fraction of borides and gamma' phase in the center of the joint decreased and increased, respectively. The high-temperature tensile test results show that the tensile strength of the joints was improved with increasing brazing temperature, and the maximum tensile strength of the joint was 766 MPa after brazing at 1290 degrees C for 60 min. Fracture observation shows that the fracture modes of the joints were the same, which belongs to the typical quasi cleavage fracture. The element distribution in the joint was homogenized to a certain extent at 1290 degrees C. The segregation of Si and Ru was found, but they were still dissolved in the gamma solid solution. The experimental results help to better understand the microstructure characteristics of the novel fourth-generation nickel-based single crystal superalloy and provide guidance for further optimizing the process parameters of the brazed joint.
KeywordSuperalloy Vacuum brazing Co-based filler alloy Mechanical properties
Funding OrganizationNational Natural Science Foundation of China ; National Key R&D Program of China ; National Science and Technology Major Project
DOI10.1007/s12540-022-01223-7
Indexed BySCI
Language英语
Funding ProjectNational Natural Science Foundation of China[51871221] ; National Key R&D Program of China[2017YFA0700704] ; National Science and Technology Major Project[2017-VI-0002-0072] ; National Science and Technology Major Project[J2019-VI-0023-0139] ; National Science and Technology Major Project[J2019-VII-0004-0144]
WOS Research AreaMaterials Science ; Metallurgy & Metallurgical Engineering
WOS SubjectMaterials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
WOS IDWOS:000805721700004
PublisherKOREAN INST METALS MATERIALS
Citation statistics
Cited Times:5[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/174255
Collection中国科学院金属研究所
Corresponding AuthorLiu, J. D.; Qiu, K. Q.
Affiliation1.Shenyang Univ Technol, Sch Mat Sci & Engn, Shenyang 110870, Peoples R China
2.Chinese Acad Sci, Shi Changxu Innovat Ctr Adv Mat, Inst Met Res, Shenyang 110016, Peoples R China
Recommended Citation
GB/T 7714
Zhang, Z. P.,Liu, J. D.,Qiu, K. Q.,et al. Effects of Brazing Temperature on Microstructure and High-Temperature Strength of Joints Using a Novel Fourth-Generation Nickel-Based Single Crystal Superalloy[J]. METALS AND MATERIALS INTERNATIONAL,2022:13.
APA Zhang, Z. P..,Liu, J. D..,Qiu, K. Q..,Huang, Y. Y..,Li, J. G..,...&Zhou, Y. Z..(2022).Effects of Brazing Temperature on Microstructure and High-Temperature Strength of Joints Using a Novel Fourth-Generation Nickel-Based Single Crystal Superalloy.METALS AND MATERIALS INTERNATIONAL,13.
MLA Zhang, Z. P.,et al."Effects of Brazing Temperature on Microstructure and High-Temperature Strength of Joints Using a Novel Fourth-Generation Nickel-Based Single Crystal Superalloy".METALS AND MATERIALS INTERNATIONAL (2022):13.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Zhang, Z. P.]'s Articles
[Liu, J. D.]'s Articles
[Qiu, K. Q.]'s Articles
Baidu academic
Similar articles in Baidu academic
[Zhang, Z. P.]'s Articles
[Liu, J. D.]'s Articles
[Qiu, K. Q.]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Zhang, Z. P.]'s Articles
[Liu, J. D.]'s Articles
[Qiu, K. Q.]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.