Preparation and performance optimization of zinc aluminate ceramic by solid-state reaction sintering

doi:10.1016/j.ceramint.2024.07.336

IMR OpenIR

	Preparation and performance optimization of zinc aluminate ceramic by solid-state reaction sintering
	Shen, Qinke 1; Hao, Jianying 1; Zhu, Zhenguo 2; Bai, Shuo 2; Wu, Jianguo 1
通讯作者	Hao, Jianying(jianyinghao@tyust.edu.cn) ; Zhu, Zhenguo(zgzhu@imr.ac.cn)
	2024-10-15
发表期刊	CERAMICS INTERNATIONAL
ISSN	0272-8842
卷号	50 期号:20 页码:39574-39580
摘要	Zinc aluminate (ZnAl2O4, 2 O 4 , ZA) ceramic plays an important role in the development of industry and technology because of its many excellent characteristics. ZA ceramic was prepared by solid-state reaction sintering at 1550 degrees C from bauxite and zinc oxide (ZnO). The effects of different mass ratios of bauxite to ZnO and milling time on the densification, linear shrinkage, porosity, strength and microstructure of ZA ceramic were investigated. It is found that as the relative content of bauxite decreases, the strength of ZA ceramic first increases and then decreases. In addition, suitable milling time is beneficial to improve the performance of ZA ceramic, but too long milling time will be detrimental to its performance. As the mixture with 1:1 of mass ratio of bauxite to ZnO is milled for 5 h, the prepared ZA ceramic has the best performance, 4.79 g/cm3 3 of bulk density, 3.53 % of apparent porosity, 177.38 MPa of flexural strength and 523.62 MPa of compressive strength.
关键词	Zinc aluminate ceramic Mass ratio Milling time Densification Mechanical properties
资助者	Applied Basic Research Project of Shanxi Province ; Taiyuan University of Science and Technology Doctoral Start-up Fund Project
DOI	10.1016/j.ceramint.2024.07.336
收录类别	SCI
语种	英语
资助项目	Applied Basic Research Project of Shanxi Province[202203021211186] ; Taiyuan University of Science and Technology Doctoral Start-up Fund Project[20212028]
WOS研究方向	Materials Science
WOS类目	Materials Science, Ceramics
WOS记录号	WOS:001308189400001
出版者	ELSEVIER SCI LTD
引用统计
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/189701
专题	中国科学院金属研究所
通讯作者	Hao, Jianying; Zhu, Zhenguo
作者单位	1.Taiyuan Univ Sci & Technol, Sch Mat Sci & Engn, Taiyuan 030024, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China
推荐引用方式 GB/T 7714	Shen, Qinke,Hao, Jianying,Zhu, Zhenguo,et al. Preparation and performance optimization of zinc aluminate ceramic by solid-state reaction sintering[J]. CERAMICS INTERNATIONAL,2024,50(20):39574-39580.
APA	Shen, Qinke,Hao, Jianying,Zhu, Zhenguo,Bai, Shuo,&Wu, Jianguo.(2024).Preparation and performance optimization of zinc aluminate ceramic by solid-state reaction sintering.CERAMICS INTERNATIONAL,50(20),39574-39580.
MLA	Shen, Qinke,et al."Preparation and performance optimization of zinc aluminate ceramic by solid-state reaction sintering".CERAMICS INTERNATIONAL 50.20(2024):39574-39580.