Behavior of 3 mol% yttria-stabilized tetragonal zirconia polycrystal film prepared by slurry spin coating

IMR OpenIR

	Behavior of 3 mol% yttria-stabilized tetragonal zirconia polycrystal film prepared by slurry spin coating
	K. F. Chen; Y. T. Tian; Z. Lu; N. Ai; X. Q. Huang; W. H. Su
	2009
发表期刊	Journal of Power Sources
ISSN	0378-7753
卷号	186 期号:1 页码:128-132
摘要	A dense and uniform 3 mol% yttria-stabilized tetragonal zirconia polycrystal (3YSZ) electrolyte film of 6 mu m in thickness was fabricated by slurry spin coating on a porous NiO/3YSZanode substrate. Composite cathodes of La(0.7)Sr(0.3)MnO(3) impregnated with Sm(0.2)Ce(0.8)O(1.9) were fabricated on the 3YSZ films. A single cell produced in this way was tested at 700, 750 and 800 degrees C with hydrogen as fuel and stationary air as oxidant. Test results revealed an open-circuit voltage of 1.04V at 800 degrees C, and maximum power density of 551.895 and 1143 mW cm(-2) at 700,750 and 800 degrees C, respectively. Impedance spectra results demonstrated that the cell performance was determined by the polarization resistance of the cathode. (c) 2008 Elsevier B.V. All rights reserved.
部门归属	[chen, kongfa; tian, yanting; lue, zhe; ai, na; huang, xiqiang; su, wenhui] harbin inst technol, ctr condensed matter sci & technol, harbin 150001, peoples r china. [su, wenhui] jilin univ, dept condensed matter phys, changchun 130022, peoples r china. [su, wenhui] int ctr mat phys, shenyang 110015, peoples r china.;lu, z (reprint author), harbin inst technol, ctr condensed matter sci & technol, harbin 150001, peoples r china;kongfachen@163.com yanting_005@163.com lvzhe@hit.edu.cn
关键词	3ysz Electrolyte Film Slurry Spin Coating Sofc Oxide Fuel-cells Ysz Electrolyte Thin-films It-sofc Fabrication Temperature Performance Membranes Ceramics Nio/ysz
URL	查看原文
WOS记录号	WOS:000262796000017
引用统计	被引频次：13[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/31827
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	K. F. Chen,Y. T. Tian,Z. Lu,et al. Behavior of 3 mol% yttria-stabilized tetragonal zirconia polycrystal film prepared by slurry spin coating[J]. Journal of Power Sources,2009,186(1):128-132.
APA	K. F. Chen,Y. T. Tian,Z. Lu,N. Ai,X. Q. Huang,&W. H. Su.(2009).Behavior of 3 mol% yttria-stabilized tetragonal zirconia polycrystal film prepared by slurry spin coating.Journal of Power Sources,186(1),128-132.
MLA	K. F. Chen,et al."Behavior of 3 mol% yttria-stabilized tetragonal zirconia polycrystal film prepared by slurry spin coating".Journal of Power Sources 186.1(2009):128-132.