Preparation and Luminescence Characteristics of BaHfO(3):Ce Nanoparticles by the Process of Solid-State Reaction

IMR OpenIR

	Preparation and Luminescence Characteristics of BaHfO(3):Ce Nanoparticles by the Process of Solid-State Reaction
	K. Yin; W. M. Ma; L. Wen; S. F. Shen; H. D. Wang; Y. F. Guo
	2009
发表期刊	Chinese Journal of Inorganic Chemistry
ISSN	1001-4861
卷号	25 期号:7 页码:1248-1253
摘要	BaHfO(3):Ce nanoparticles were synthesized by the process of solid-state reaction. Both XRD and SEM were adopted to analyze the phase change and the characteristics of BaHfO(3):Ce nano-powders during calcining process. Excitation and emission spectra were analyzed separately with the fluorescence photometer. The result shows that the average diameter of the BaHfO(3):Ce nano-powders being approximate to spherical morphology is about 30 nm and the powders have good dispersibility after calcining at 1000 degrees C for 2 h. It also shows that there is no change happened on the cubic crystal structure even though a little amount of Ce(3+) ion added to the powders can lead to the lattice distortion of BaHfO(3) matrix material. The excitation spectrum of BaHfO(3): Ce nanoparticles has two excitation peaks separately at 396 nm and 446 nm points. The emission spectrum excited by the 396 nm light consists of two emission bands, peaking at 531 nm and 591 run, respectively, the emission character of which changes from the 5d ->(2)F(5/2) to 5d ->(2)F(7/2) transitions of Ce(3+) cation. When the emission spectrum is excited by the 446 nm light, only one wide emission peak at 591 nm point exists and the other one at around 531 nm becomes flat. When the Ce(3+) dopant content is 0.9%(molar fraction), the figure of the emission peak reaches its highest point. This figure, however, drops when The Ce(3+) dopant content is 1.1%( molar fraction), which is resulted from the concentraction quenching.
部门归属	[yin kai; ma wei-min] shenyang inst chem technol, sch mat sci & engn, shenyang 110142, peoples r china. [yin kai; shen shi-fei; wang hua-dong; guo yi-fen] shenyang univ, coll mech engn, shenyang 110044, peoples r china. [wen lei] chinese acad sci, shenyang natl lab mat sci, inst met res, shenyang 110016, peoples r china.;ma, wm (reprint author), shenyang inst chem technol, sch mat sci & engn, shenyang 110142, peoples r china;maweimin56@163.com
关键词	Scintillant Bahfo(3):Ce Nanoparticles Solid-state Reaction Process Excitation Spectrum Emission Spectrum Combustion Synthesis Photoluminescence Phosphors Y2o3-eu Ca Sr Ba Nanophosphors Fabrication Ceramics
URL	查看原文
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/32506
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	K. Yin,W. M. Ma,L. Wen,et al. Preparation and Luminescence Characteristics of BaHfO(3):Ce Nanoparticles by the Process of Solid-State Reaction[J]. Chinese Journal of Inorganic Chemistry,2009,25(7):1248-1253.
APA	K. Yin,W. M. Ma,L. Wen,S. F. Shen,H. D. Wang,&Y. F. Guo.(2009).Preparation and Luminescence Characteristics of BaHfO(3):Ce Nanoparticles by the Process of Solid-State Reaction.Chinese Journal of Inorganic Chemistry,25(7),1248-1253.
MLA	K. Yin,et al."Preparation and Luminescence Characteristics of BaHfO(3):Ce Nanoparticles by the Process of Solid-State Reaction".Chinese Journal of Inorganic Chemistry 25.7(2009):1248-1253.