| Studies of impedance models and water transport behaviours of epoxy coating at hydrostatic pressure of seawater |
| J. Liu; X. B. Li; J. Wang; T. Y. Luo; X. M. Wang
|
| 2013
|
| 发表期刊 | Progress in Organic Coatings
 |
| ISSN | 0300-9440
|
| 卷号 | 76期号:7-8页码:1075-1081 |
| 摘要 | In simulated deep-sea environment, the evolution of impedance models and water transport behaviours of epoxy coating on 907A steel surface were studied by electrochemical impedance spectroscopy (EIS). By the fitting analysis of EIS, three equivalent electrical circuits (EEC) were proposed to the epoxy coating/907A steel system at 25 atm hydrostatic pressure for different immersion stages: good barrier property of the coating (Circuit A), active corrosion period at the beginning (Circuit B), and finally emergency of diffusion impedance (Circuit C). The evolution of coating capacitance indicated that water transport followed the Fickian diffusion behaviour during the initial stage at 25 atm hydrostatic pressure and at atmospheric pressure. High pressure accelerated diffusion rates of seawater into epoxy coatings, this shortened the period of water uptake of the coating that reached saturation. The similar chemical structures of epoxy coatings at two kinds of hydrostatic pressure were found from the Fourier transform infrared spectroscopy (Fr-IR) - attenuated total reflection (ATR) measurements. High pressure of seawater accelerated the coating physical failure, and chemical structures of the coating did not change during the experiment. (C) 2013 Elsevier B.V. All rights reserved. |
| 部门归属 | [liu jie
; luo tian-yuan] southwest technol & engn res inst, chongqing 400039, peoples r china. [liu jie
; wang xiao-ming] nanjing univ sci & technol, sch mech engn, nanjing 210094, jiangsu, peoples r china. [li xiang-bo] state key lab marine corros & protect, qingdao 266071, peoples r china. [wang jia] state key lab corros & protect, shenyang 110016, peoples r china.
; liu, j (reprint author), southwest technol & engn res inst, chongqing 400039, peoples r china.
; liujie6573@163.com
|
| 关键词 | Epoxy Coating
Impedance Models
Water Transport
Hydrostatic Pressure
Of Seawater
Nacl Solution
Corrosion Protection
Organic Coatings
Aluminum-alloys
Coated Metals
Paint Systems
Eis
Spectroscopy
Diffusion
Films
|
| URL | 查看原文
|
| 语种 | 英语
|
| 文献类型 | 期刊论文
|
| 条目标识符 | http://ir.imr.ac.cn/handle/321006/71368
|
| 专题 | 中国科学院金属研究所
|
推荐引用方式
GB/T 7714 |
J. Liu,X. B. Li,J. Wang,et al. Studies of impedance models and water transport behaviours of epoxy coating at hydrostatic pressure of seawater[J]. Progress in Organic Coatings,2013,76(7-8):1075-1081.
|
| APA |
J. Liu,X. B. Li,J. Wang,T. Y. Luo,&X. M. Wang.(2013).Studies of impedance models and water transport behaviours of epoxy coating at hydrostatic pressure of seawater.Progress in Organic Coatings,76(7-8),1075-1081.
|
| MLA |
J. Liu,et al."Studies of impedance models and water transport behaviours of epoxy coating at hydrostatic pressure of seawater".Progress in Organic Coatings 76.7-8(2013):1075-1081.
|
修改评论