	Anisotropic friction behaviour of highly oriented pyrolytic graphite
	J. K. Xiao; L. Zhang; K. C. Zhou; J. G. Li; X. L. Xie; Z. Y. Li
	2013
发表期刊	Carbon
ISSN	0008-6223
卷号	65 页码:53-62
摘要	Friction tests on two surfaces of highly oriented pyrolytic graphite that are parallel and perpendicular to the direction of the graphite basal plane were performed under various test conditions. The average friction coefficient value of the perpendicular surface (0.25) is higher than that of the parallel surface (0.1). The friction coefficient of both parallel and perpendicular surfaces decline when the environment is changed from wet air to wet nitrogen and the trend is more pronounced for the perpendicular surface. The perpendicular worn surface has been observed to be much rougher and owns more edge faces than the parallel worn surface. The amount of dangling bonds and chemisorbed oxygen measured on both surfaces after friction is quite different. The influence of atmosphere on the friction of graphite is attributed to the chemical reaction of dangling bonds with gases, which can affect the adhesive force of the two contact surfaces. The amount of dangling bonds generated on the sliding surface is confirmed to impact the sensitivity of graphite to gases during friction. (C) 2013 Elsevier Ltd. All rights reserved.
部门归属	[xiao, jinkun ; zhang, lei ; zhou, kechao ; xie, xinlin ; li, zhiyou] cent s univ, state key lab powder met, changsha 410083, peoples r china. [li, jianguo] chinese acad sci, inst met res, shenyang 110016, peoples r china. ; zhang, l (reprint author), cent s univ, state key lab powder met, changsha 410083, peoples r china. ; csuzhanglei@gmail.com
关键词	Raman-spectroscopy Diamond Surfaces Carbon Materials Wear Debris Composites Graphene Transition Disorder Braking Films
URL	查看原文
语种	英语
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/71593
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	J. K. Xiao,L. Zhang,K. C. Zhou,et al. Anisotropic friction behaviour of highly oriented pyrolytic graphite[J]. Carbon,2013,65:53-62.
APA	J. K. Xiao,L. Zhang,K. C. Zhou,J. G. Li,X. L. Xie,&Z. Y. Li.(2013).Anisotropic friction behaviour of highly oriented pyrolytic graphite.Carbon,65,53-62.
MLA	J. K. Xiao,et al."Anisotropic friction behaviour of highly oriented pyrolytic graphite".Carbon 65(2013):53-62.