Preparation, Microstructure, and Mechanical Properties of Nb4AlC3-Nb-5(Si, Al)(3) Composites

IMR OpenIR

	Preparation, Microstructure, and Mechanical Properties of Nb4AlC3-Nb-5(Si, Al)(3) Composites
	L. Y. Zheng; J. Y. Wang; J. X. Chen; M. Y. Liu; Y. J. Sun; Y. C. Zhou
	2013
发表期刊	Journal of the American Ceramic Society
ISSN	0002-7820
卷号	96 期号:2 页码:365-368
摘要	Niobium aluminum carbide (Nb4AlC3), as a member of the MAX phases, can retain its stiffness and strength up to over 1400 degrees C, however, the strength at room temperature is relatively low. In this work, Nb5(Si, Al)3 was used to strengthen Nb4AlC3. Nb4AlC3Nb5(Si, Al)3 composites with different amount of Nb5(Si, Al)3 were synthesized from the elemental powders by in situ hot-pressing/solidliquid reaction synthesis process. The RT flexural strength was significantly improved from 370MPa of monolithic Nb4AlC3 to 432MPa of Nb4AlC3-15vol% Nb5(Si, Al)3 composite without the degradation of its high-temperature mechanical properties. While a slightly decrease in fracture toughness occurs with the increment of Nb5(Si, Al)3 content. Meanwhile, Transmission electron microscopy (TEM) observations reveal that the interfaces between Nb4AlC3/Nb4AlC3, Nb4AlC3/Nb5(Si, Al)3, and Nb5(Si, Al)3/Nb5(Si, Al)3 are free of amorphous layers, which is also beneficial to its high-temperature mechanical properties.
部门归属	[zheng, l. y. ; wang, j. y. ; chen, j. x. ; liu, m. y.] chinese acad sci, inst met res, shenyang natl lab mat sci, shenyang 110016, peoples r china. [zheng, l. y.] chinese acad sci, grad sch, beijing 100039, peoples r china. [sun, y. j. ; zhou, y. c.] arimpt, sci & technol adv funct composite lab, beijing 100076, peoples r china. ; zhou, yc (reprint author), amer ceram soc, westerville, oh 43086 usa. ; yczhou714@gmail.com
关键词	Situ Reaction Synthesis High-temperature Nb4alc3 Fabrication Phases Room
URL	查看原文
语种	英语
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/71724
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	L. Y. Zheng,J. Y. Wang,J. X. Chen,et al. Preparation, Microstructure, and Mechanical Properties of Nb4AlC3-Nb-5(Si, Al)(3) Composites[J]. Journal of the American Ceramic Society,2013,96(2):365-368.
APA	L. Y. Zheng,J. Y. Wang,J. X. Chen,M. Y. Liu,Y. J. Sun,&Y. C. Zhou.(2013).Preparation, Microstructure, and Mechanical Properties of Nb4AlC3-Nb-5(Si, Al)(3) Composites.Journal of the American Ceramic Society,96(2),365-368.
MLA	L. Y. Zheng,et al."Preparation, Microstructure, and Mechanical Properties of Nb4AlC3-Nb-5(Si, Al)(3) Composites".Journal of the American Ceramic Society 96.2(2013):365-368.