Enhanced in vitro biocompatibility/bioactivity of biodegradable Mg-Zn-Zr alloy by micro-arc oxidation coating contained Mg2SiO4
X. M. Yang; M. Li; X. Lin; L. L. Tan; G. B. Lan; L. H. Li; Q. S. Yin; H. Xia; Y. Zhang; K. Yang
2013
Source PublicationSurface & Coatings Technology
ISSN0257-8972
Volume233Pages:65-73
AbstractThere is a great attraction to apply magnesium alloy as an orthopedic implant material due to its biodegradable feature and suitable mechanical properties. In order to further improve the biocompatibility of magnesium alloy, a Mg2SiO4-containing micro-arc oxidation (MAO) coating was generated on ZK60 magnesium alloy, in this study. The surface characterization by SEM, XRD and EDS showed that a rough and porous reaction layer with major composition of O, Mg and Si was formed on the surface of ZK60 alloy. The result of polarization test showed that the MAO coating significantly enhanced the corrosion resistance of biodegradable ZK60 alloy. In vitro biocompatibility/bioactivity evaluation of the MAO-coated alloy compared with the naked alloy was performed using murine bone marrow stem cells (BMSCs). The results revealed that the extract of MAO-coated alloy had no obvious cytotoxicity during the 5 days culturing, and the surface of MAO coating exhibited a better cell adhesion and affinity. Alkaline phosphatase (ALP) activity assay demonstrated that the ALP level of the BMSCs in the extract of MAO-coated alloy was much higher than that of the naked alloy, indicating that the release of Mg and Si ions from the coating was beneficial for the differentiation of BMSCs. Result of blood hemolysis test showed that the MAO coating group had a drastically decreased hemolytic ratio (1.04%) compared with the naked alloy group (28.78%) (p<0.01), meaning a great improvement of hemocompatibility. In conclusion, the results of this study suggested that the Mg2SiO4-containing MAO coating is an effective way to improve the biocompatibility/bioactivity of magnesium alloys. (C) 2013 Elsevier B.V. All rights reserved.
description.department[yang, xiaoming] southern med univ, guangzhou 510515, guangdong, peoples r china. [yang, xiaoming ; li, mei ; lan, guobo ; li, lihua ; yin, qingshui ; xia, hong ; zhang, yu] guangzhou mil command, guangzhou gen hosp, orthoped hosp, guangzhou 510010, guangdong, peoples r china. [lin, xiao ; tan, lili ; yang, ke] chinese acad sci, inst met res, shenyang 110016, peoples r china. ; xia, h (reprint author), guangzhou mil command, guangzhou gen hosp, orthoped hosp, 111 liuhua rd, guangzhou 510010, guangdong, peoples r china. ; gzxiahong2@126.com ; luck_2001@126.com ; kyang@imr.ac.cn
KeywordMg2sio4 Micro-arc Oxidation Biocompatibility Bioactivity Biodegradable Magnesium In Vitro Simulated Body-fluid Magnesium Alloys Osteoblastic Differentiation Orthosilicic Acid Ceramic Coatings Corrosion Surface Adhesion Behavior Silicon
URL查看原文
Language英语
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/72361
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
X. M. Yang,M. Li,X. Lin,et al. Enhanced in vitro biocompatibility/bioactivity of biodegradable Mg-Zn-Zr alloy by micro-arc oxidation coating contained Mg2SiO4[J]. Surface & Coatings Technology,2013,233:65-73.
APA X. M. Yang.,M. Li.,X. Lin.,L. L. Tan.,G. B. Lan.,...&K. Yang.(2013).Enhanced in vitro biocompatibility/bioactivity of biodegradable Mg-Zn-Zr alloy by micro-arc oxidation coating contained Mg2SiO4.Surface & Coatings Technology,233,65-73.
MLA X. M. Yang,et al."Enhanced in vitro biocompatibility/bioactivity of biodegradable Mg-Zn-Zr alloy by micro-arc oxidation coating contained Mg2SiO4".Surface & Coatings Technology 233(2013):65-73.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[X. M. Yang]'s Articles
[M. Li]'s Articles
[X. Lin]'s Articles
Baidu academic
Similar articles in Baidu academic
[X. M. Yang]'s Articles
[M. Li]'s Articles
[X. Lin]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[X. M. Yang]'s Articles
[M. Li]'s Articles
[X. Lin]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.