|In Situ Growth Process of Mg-Al Hydrotalcite Conversion Film on AZ31 Mg Alloy|
|J.; Song Chen, Y. W.; Shan, D. Y.; Han, E. H.
|Source Publication||Journal of Materials Science & Technology
|Abstract||In this study, an environment-friendly hydrotalcite film has been deposited on AZ31 Mg alloy by a two-step technique. To improve conversion film technique and control film properties, batch studies have been carried out to address various process parameters such as immersion time, pH value, and temperature of the treatment solution. The morphologies and chemical composition were characterized by scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDS). The corrosion resistance of the samples with the various final films was then further compared by polarization curves. It can be concluded from the results that, at low value of pH, temperature, or long deposition time, the precursor film is mainly composed of a cracked layer. The transformation of hydrotalcite film is largely influenced by the pH value. There are optimum values of pH, temperature of the coating bath and immersion time for the film formation process to achieve the best quality and corrosion resistance of the hydrotalcite film. The optimum process is as follows: the sample is first immersed in the pretreatment solution with a pH value of about 8 at a temperature of 60 degrees C for 30 min to form a precursor film and then this precursor film is immersed into the post treatment solution with a pH of 10.5 at 80 degrees C for 1.5 h to obtain the Mg-Al hydrotalcite conversion film. Copyright (C) 2015, The editorial office of Journal of Materials Science & Technology. Published by Elsevier Limited. All rights reserved.|
|description.department||[chen, jun] xihua univ, ctr adv mat & energy, chengdu 610039, peoples r china. [chen, jun
; song, yingwei
; shan, dayong
; han, en-hou] chinese acad sci, inst met res, environm corros ctr, shenyang 110016, peoples r china.
; chen, j (reprint author), xihua univ, ctr adv mat & energy, chengdu 610039, peoples r china.
J.,Song Chen, Y. W.,Shan, D. Y.,et al. In Situ Growth Process of Mg-Al Hydrotalcite Conversion Film on AZ31 Mg Alloy[J]. Journal of Materials Science & Technology,2015,31(4):384-390.
J.,Song Chen, Y. W.,Shan, D. Y.,&Han, E. H..(2015).In Situ Growth Process of Mg-Al Hydrotalcite Conversion Film on AZ31 Mg Alloy.Journal of Materials Science & Technology,31(4),384-390.
J.,et al."In Situ Growth Process of Mg-Al Hydrotalcite Conversion Film on AZ31 Mg Alloy".Journal of Materials Science & Technology 31.4(2015):384-390.
|Files in This Item:||
||There are no files associated with this item.
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.