Damage Tolerance and Extensive Plastic Deformation of -Yb2Si2O7 from Room to High Temperatures
Tian, Zhilin; Zheng, Liya; Wang, Jiemin; Yang, Jinbo; Yang, Guang; Wang, Jingyang; jywang@imr.ac.cn
2015
Source PublicationJOURNAL OF THE AMERICAN CERAMIC SOCIETY
ISSN0002-7820
Volume98Issue:9Pages:2843-2851
Abstractbeta-Yb2Si2O7 is a promising environmental barrier coating (EBC) material and recently attracted attention for its damage tolerance. To investigate the mechanisms of its damage tolerance and possible plasticity, dense -Yb2Si2O7 sample was synthesized by insitu reaction/hot-pressing method, and its mechanical properties were measured from room to high temperatures. The low magnitudes of hardness to Young's modulus ratio H-V/E, shear modulus to bulk modulus ratio G/B, and high fracture toughness to strength ratio K-IC/sigma provide evidences of damage tolerance of -Yb2Si2O7. -Yb2Si2O7 exhibits extensive plastic deformation in Hertzian contact tests at both room and high temperatures. Transmission electron microscopy (TEM) observations show that the deformation mechanisms are different at low and high temperatures. Deformation twinning and parallel dislocation arrangement occur in plastic deformation at room temperature. Above the brittle-to-ductile transition temperature (between 1200 degrees C and 1300 degrees C), plastic deformation brings out extensive slip and climb of dislocations, while twinning is seldom observed. Measurement of temperature-dependent dynamic Young's modulus demonstrates excellent elastic stiffness retention up to 1300 degrees C.
description.department[tian, zhilin ; zheng, liya ; wang, jiemin ; yang, jinbo ; yang, guang ; wang, jingyang] chinese acad sci, inst met res, shenyang natl lab mat sci, shenyang 110016, peoples r china ; [tian, zhilin ; zheng, liya ; yang, guang] univ chinese acad sci, beijing 100049, peoples r china ; [yang, guang] northeastern univ, sch met & mat, shenyang 110819, peoples r china
Funding OrganizationNatural Sciences Foundation of China [51032006, 51372252]
Indexed Bysci
Language英语
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/74704
Collection中国科学院金属研究所
Corresponding Authorjywang@imr.ac.cn
Recommended Citation
GB/T 7714
Tian, Zhilin,Zheng, Liya,Wang, Jiemin,et al. Damage Tolerance and Extensive Plastic Deformation of -Yb2Si2O7 from Room to High Temperatures[J]. JOURNAL OF THE AMERICAN CERAMIC SOCIETY,2015,98(9):2843-2851.
APA Tian, Zhilin.,Zheng, Liya.,Wang, Jiemin.,Yang, Jinbo.,Yang, Guang.,...&jywang@imr.ac.cn.(2015).Damage Tolerance and Extensive Plastic Deformation of -Yb2Si2O7 from Room to High Temperatures.JOURNAL OF THE AMERICAN CERAMIC SOCIETY,98(9),2843-2851.
MLA Tian, Zhilin,et al."Damage Tolerance and Extensive Plastic Deformation of -Yb2Si2O7 from Room to High Temperatures".JOURNAL OF THE AMERICAN CERAMIC SOCIETY 98.9(2015):2843-2851.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Tian, Zhilin]'s Articles
[Zheng, Liya]'s Articles
[Wang, Jiemin]'s Articles
Baidu academic
Similar articles in Baidu academic
[Tian, Zhilin]'s Articles
[Zheng, Liya]'s Articles
[Wang, Jiemin]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Tian, Zhilin]'s Articles
[Zheng, Liya]'s Articles
[Wang, Jiemin]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.