Influence of Zn interlayer addition on microstructure and mechanical properties of friction stir welded AZ31 Mg alloy
Xu, R. Z.; Ni, D. R.; Yang, Q.; Liu, C. Z.; Ma, Z. Y.; zyma@imr.ac.cn
2015
Source PublicationJOURNAL OF MATERIALS SCIENCE
ISSN0022-2461
Volume50Issue:12Pages:4160-4173
Abstract2.4-mm-thick AZ31 Mg alloy sheets were friction stir spot welded without and with the addition of Zn interlayers ranging from 0.04 to 0.16 mm in thickness. For the joints without Zn interlayers, although the loads of the joints could be increased by changing the end surface geometry and size of the shoulders, the small bonded area and hook defects limited further increase of joint loads. For the joints with Zn interlayers, the Zn interlayer reacted with the Mg substrate, forming a Mg-Zn brazed zone composed of complex Mg-Zn intermetallics and a thin strip of (alpha-Mg + MgZn) eutectoid structure, thereby increasing the bonded area and reducing the hook defects of joints at the same time. As a result, the maximum joint load increased from 2.7 to 5.2 kN using a 10-mm-diameter concave shoulder with a 0.12-mm-thick Zn interlayer. A thicker interlayer resulted in a significant increase in the thickness of the thin strip in the hook region, and a thinner interlayer led to the formation of more defects due to intense diffusion reactions, thereby reducing the joint loads.
description.department[xu, r. z. ; ni, d. r. ; yang, q. ; ma, z. y.] chinese acad sci, inst met res, shenyang natl lab mat sci, shenyang 110016, peoples r china ; [xu, r. z. ; liu, c. z.] shenyang aerosp univ, coll mat sci & engn, shenyang 110136, peoples r china
Funding OrganizationNational R&D Program of China [2011BAE22B05]; National Natural Science Foundation of China [51371179, 51331008]
Indexed Bysci
Language英语
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/74921
Collection中国科学院金属研究所
Corresponding Authorzyma@imr.ac.cn
Recommended Citation
GB/T 7714
Xu, R. Z.,Ni, D. R.,Yang, Q.,et al. Influence of Zn interlayer addition on microstructure and mechanical properties of friction stir welded AZ31 Mg alloy[J]. JOURNAL OF MATERIALS SCIENCE,2015,50(12):4160-4173.
APA Xu, R. Z.,Ni, D. R.,Yang, Q.,Liu, C. Z.,Ma, Z. Y.,&zyma@imr.ac.cn.(2015).Influence of Zn interlayer addition on microstructure and mechanical properties of friction stir welded AZ31 Mg alloy.JOURNAL OF MATERIALS SCIENCE,50(12),4160-4173.
MLA Xu, R. Z.,et al."Influence of Zn interlayer addition on microstructure and mechanical properties of friction stir welded AZ31 Mg alloy".JOURNAL OF MATERIALS SCIENCE 50.12(2015):4160-4173.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Xu, R. Z.]'s Articles
[Ni, D. R.]'s Articles
[Yang, Q.]'s Articles
Baidu academic
Similar articles in Baidu academic
[Xu, R. Z.]'s Articles
[Ni, D. R.]'s Articles
[Yang, Q.]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Xu, R. Z.]'s Articles
[Ni, D. R.]'s Articles
[Yang, Q.]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.