Study of the processing map and hot deformation behavior of a Cu-bearing 317LN austenitic stainless steel
Xi, Tong; Yang, Chunguang; Shahzad, M. Babar; Yang, Ke; kyang@imr.ac.cn
2015
Source PublicationMATERIALS & DESIGN
ISSN0261-3069
Volume87Pages:303-312
AbstractThe hot-working behavior of a Cu-bearing 317LN austenitic stainless steel (317LN-Cu) was investigated in the 950-1150 degrees C temperature and 0.01-10 s(-1) strain rate range, respectively. The effects of different deformation parameters and optimum hot-working window were respectively characterized through analyzing flow stress curves, constitutive equations, processing maps and microstructures. The critical strain for dynamic recrystallization (DRX) was determined by the inflection point on theta-sigma and -partial derivative theta/partial derivative sigma-sigma curves. The peak stress was found to increase with decrease in temperature and increase in strain rate. Typical signs of DRX over a wide range of temperatures and strain rates were observed on the flow stress curves. The power dissipation maps in the strain range of 0.1-0.4 were basically similar, indicating the insignificant effect of strain on the power dissipation maps of 317LN-Cu. However, the instability maps showed strong strain sensitivity with increasing strain, which was attributed to the flow localization. The optimum hot-working window for 317L14-Cu was obtained in the temperature range 1100-1120 degrees C and strain rate range 0.01-0.018 s(-1), with a peak efficiency of 38%. Microstructural analysis revealed fine and homogenized recrystallized grains in this domain. (C) 2015 Elsevier Ltd. All rights reserved.
description.department[xi, tong] dalian univ technol, sch mat sci & engn, dalian 116024, peoples r china ; [xi, tong ; yang, chunguang ; shahzad, m. babar ; yang, ke] chinese acad sci, inst met res, shenyang 110016, peoples r china
KeywordCu-bearing Stainless Steel Hot Compression Processing Maps Constitutive Equation Dynamic Recystallization
Funding OrganizationNational Basic Research Program of China [2012CB619101]; National Natural Science Foundation of China [51371168]; Shenyang National Lab for Materials Science; Foundation of Jiangsu Collaborative Innovation Center of Biomedical Functional Materials
Indexed Bysci
Language英语
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/75142
Collection中国科学院金属研究所
Corresponding Authorkyang@imr.ac.cn
Recommended Citation
GB/T 7714
Xi, Tong,Yang, Chunguang,Shahzad, M. Babar,et al. Study of the processing map and hot deformation behavior of a Cu-bearing 317LN austenitic stainless steel[J]. MATERIALS & DESIGN,2015,87:303-312.
APA Xi, Tong,Yang, Chunguang,Shahzad, M. Babar,Yang, Ke,&kyang@imr.ac.cn.(2015).Study of the processing map and hot deformation behavior of a Cu-bearing 317LN austenitic stainless steel.MATERIALS & DESIGN,87,303-312.
MLA Xi, Tong,et al."Study of the processing map and hot deformation behavior of a Cu-bearing 317LN austenitic stainless steel".MATERIALS & DESIGN 87(2015):303-312.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Xi, Tong]'s Articles
[Yang, Chunguang]'s Articles
[Shahzad, M. Babar]'s Articles
Baidu academic
Similar articles in Baidu academic
[Xi, Tong]'s Articles
[Yang, Chunguang]'s Articles
[Shahzad, M. Babar]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Xi, Tong]'s Articles
[Yang, Chunguang]'s Articles
[Shahzad, M. Babar]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.