Microstructure, Residual Strain and Stress Behavior in 316L Heat-Affected Zone

IMR OpenIR

	Microstructure, Residual Strain and Stress Behavior in 316L Heat-Affected Zone
	Ming, HL; Zhang, ZM; Xiu, PY; Wang, JQ; Han, EH; Ke, W; Su, MX; Wang, JQ (reprint author), Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Liaoning Key Lab Safety & Assessment Tech Nucl Ma, Shenyang 110016, Peoples R China.
	2016-09-01
发表期刊	ACTA METALLURGICA SINICA-ENGLISH LETTERS
ISSN	1006-7191
卷号	29 期号:9 页码:848-858
摘要	Austenitic stainless steels are usually chosen to make many components of nuclear power plants (NPPs). However, their microstructure in the heat-affected zone (HAZ) will change during the welding process. Some failures of the weld joints, mainly stress corrosion cracking (SCC), have been found to be located in the HAZ. In this research, the microstructure, micro-hardness, residual strain and SCC behavior at different locations of the 316L HAZ cut from a safe end dissimilar metal weld joint were studied. However, traditional optical microscope observation could not find any microstructural difference between the HAZ and the base metal, higher residual strain and micro-hardness, and higher fraction of random high-angle grain boundaries were found in the HAZ than in the base metal when studied by using electron back-scattering diffraction scanning and micro-hardness test. What's more, the residual strain, the micro-hardness and the fraction of random grain boundaries decreased, while the fraction of coincidence site lattice grain boundaries increased with increasing the distance from the fusion boundary in 316L HAZ. Creviced bent beam test was applied to evaluate the SCC susceptibility at different locations of 316L HAZ and base metal. It was found that the HAZ had higher SCC susceptibility than the base metal and SCC resistance increased when increasing the distance from the fusion boundary in 316L HAZ.
部门归属	[ming, hong-liang ; zhang, zhi-ming ; xiu, peng-yuan ; wang, jian-qiu ; han, en-hou ; ke, wei] chinese acad sci, inst met res, key lab nucl mat & safety assessment, liaoning key lab safety & assessment tech nucl ma, shenyang 110016, peoples r china ; [ming, hong-liang] univ chinese acad sci, beijing 100049, peoples r china ; [su, ming-xing] shanghai res ctr weld & detect engn tech nucl equ, shanghai 201306, peoples r china
关键词	Austenitic Stainless Steels Heat-affected Zone Microstructure Ebsd Residual Strain Stress Corrosion Cracking
学科领域	Metallurgy & Metallurgical Engineering
资助者	National Natural Science Foundation of China [51301183]; Science and Technology Commission of Shanghai Municipality, Shanghai, China [14DZ2250300]
收录类别	sci
语种	英语
WOS记录号	WOS:000385336400009
引用统计	被引频次：23[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/76276
专题	中国科学院金属研究所
通讯作者	Wang, JQ (reprint author), Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Liaoning Key Lab Safety & Assessment Tech Nucl Ma, Shenyang 110016, Peoples R China.
推荐引用方式 GB/T 7714	Ming, HL,Zhang, ZM,Xiu, PY,et al. Microstructure, Residual Strain and Stress Behavior in 316L Heat-Affected Zone[J]. ACTA METALLURGICA SINICA-ENGLISH LETTERS,2016,29(9):848-858.
APA	Ming, HL.,Zhang, ZM.,Xiu, PY.,Wang, JQ.,Han, EH.,...&Wang, JQ .(2016).Microstructure, Residual Strain and Stress Behavior in 316L Heat-Affected Zone.ACTA METALLURGICA SINICA-ENGLISH LETTERS,29(9),848-858.
MLA	Ming, HL,et al."Microstructure, Residual Strain and Stress Behavior in 316L Heat-Affected Zone".ACTA METALLURGICA SINICA-ENGLISH LETTERS 29.9(2016):848-858.