The effect of annealing on microstructure and tensile properties of Ti-22Al-25Nb electron beam weld joint
Chen, W; Chen, ZY; Wu, CC; Li, JW; Tang, ZY; Wang, QJ; Chen, W (reprint author), Beijing Aeronaut Mfg Technol Res Inst, Power Beam Proc Lab, Beijing 100024, Peoples R China.
2016-08-01
Source PublicationINTERMETALLICS
ISSN0966-9795
Volume75Pages:8-14
AbstractThis study investigated the microstructure evolution and tensile properties of Ti-22Al-25Nb EBW joints. The fusion zone of the as-welded joint exhibited a fully B2 microstructure. Widmanstatten O particles precipitated out of B2 matrix after annealing and their size increased within a temperature range from 750 degrees C to 900 degrees C. In the heat affected zone, there was a transition of microstructure moving away from the fusion zone towards the base material. Strength and elongation of the as-welded sample were significantly improved after annealing, which was attributed to the strengthening effect of O precipitates and the slip transmission between O and B2 phases. Samples tensile tested at 650 degrees C all failed within the fusion zone and exhibited intergranular failure instead of transgranular failure at room temperature. The room temperature strength and hardness of the joints decreased with annealing temperature due to the coarsening of O precipitates. At 650 degrees C, failure occurred by intergranular fracture in the fusion zone and the joint strength of all annealed samples was similar due to similar B2 grain boundary strength. (C) 2016 Elsevier Ltd. All rights reserved.
description.department[chen, w. ; li, j. w. ; tang, z. y.] beijing aeronaut mfg technol res inst, power beam proc lab, beijing 100024, peoples r china ; [chen, z. y. ; wu, c. c. ; wang, q. j.] chinese acad sci, inst met res, shenyang 110016, peoples r china
KeywordIntermetallics Ti2alnb Electron Beam Welding Microstructure Tensile Properties
Subject AreaChemistry, Physical ; Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
Funding OrganizationPower Beam Processing Laboratory Research Fund
Indexed Bysci
Language英语
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/76316
Collection中国科学院金属研究所
Corresponding AuthorChen, W (reprint author), Beijing Aeronaut Mfg Technol Res Inst, Power Beam Proc Lab, Beijing 100024, Peoples R China.
Recommended Citation
GB/T 7714
Chen, W,Chen, ZY,Wu, CC,et al. The effect of annealing on microstructure and tensile properties of Ti-22Al-25Nb electron beam weld joint[J]. INTERMETALLICS,2016,75:8-14.
APA Chen, W.,Chen, ZY.,Wu, CC.,Li, JW.,Tang, ZY.,...&Chen, W .(2016).The effect of annealing on microstructure and tensile properties of Ti-22Al-25Nb electron beam weld joint.INTERMETALLICS,75,8-14.
MLA Chen, W,et al."The effect of annealing on microstructure and tensile properties of Ti-22Al-25Nb electron beam weld joint".INTERMETALLICS 75(2016):8-14.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Chen, W]'s Articles
[Chen, ZY]'s Articles
[Wu, CC]'s Articles
Baidu academic
Similar articles in Baidu academic
[Chen, W]'s Articles
[Chen, ZY]'s Articles
[Wu, CC]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Chen, W]'s Articles
[Chen, ZY]'s Articles
[Wu, CC]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.