	Stress corrosion cracking of fusion boundary for 316L/52M dissimilar metal weld joints in borated and lithiated high temperature water
	Zhu, Ruolin; Wang, Jianqiu; Zhang, Zhiming; Han, En-Hou; Wang, JQ (reprint author), Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Peoples R China.
	2017-05-15
发表期刊	CORROSION SCIENCE
ISSN	0010-938X
卷号	120 页码:219-230
摘要	The stress corrosion cracking (SCC) crack growth rates (CGRs) at the fusion boundary (FB) for 316L/52M weld joints were measured using direct current potential drop systems in borated and lithiated high temperature water. The cracks propagated along the FB and were blocked after propagating into the composition transient zone. The cracking mode is both intergranular and transgranular. The CGRs at the FB are similar to those in the heat-affected zone (HAZ) in oxygenated water, but slightly higher than those in the HAZ in hydrogenated water. The temperature dependences of CGR in both hydrogenated and oxygenated water are discussed. (C) 2017 Elsevier Ltd. All rights reserved.; The stress corrosion cracking (SCC) crack growth rates (CGRs) at the fusion boundary (FB) for 316L/52M weld joints were measured using direct current potential drop systems in borated and lithiated high temperature water. The cracks propagated along the FB and were blocked after propagating into the composition transient zone. The cracking mode is both intergranular and transgranular. The CGRs at the FB are similar to those in the heat-affected zone (HAZ) in oxygenated water, but slightly higher than those in the HAZ in hydrogenated water. The temperature dependences of CGR in both hydrogenated and oxygenated water are discussed. (C) 2017 Elsevier Ltd. All rights reserved.
部门归属	[zhu, ruolin ; wang, jianqiu ; zhang, zhiming ; han, en-hou] chinese acad sci, inst met res, key lab nucl mat & safety assessment, shenyang 110016, peoples r china ; [zhu, ruolin] univ chinese acad sci, 19 yuquan rd, beijing 100049, peoples r china
关键词	Stainless Steel Nickel Sem Welding Stress Corrosion
学科领域	Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
资助者	CAS [QYZDY-SSW-JSC012]; National Natural Science Foundation of China [51301183]
收录类别	SCI
语种	英语
WOS记录号	WOS:000401378100020
引用统计	被引频次：31[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/78137
专题	中国科学院金属研究所
通讯作者	Wang, JQ (reprint author), Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Peoples R China.
推荐引用方式 GB/T 7714	Zhu, Ruolin,Wang, Jianqiu,Zhang, Zhiming,et al. Stress corrosion cracking of fusion boundary for 316L/52M dissimilar metal weld joints in borated and lithiated high temperature water[J]. CORROSION SCIENCE,2017,120:219-230.
APA	Zhu, Ruolin,Wang, Jianqiu,Zhang, Zhiming,Han, En-Hou,&Wang, JQ .(2017).Stress corrosion cracking of fusion boundary for 316L/52M dissimilar metal weld joints in borated and lithiated high temperature water.CORROSION SCIENCE,120,219-230.
MLA	Zhu, Ruolin,et al."Stress corrosion cracking of fusion boundary for 316L/52M dissimilar metal weld joints in borated and lithiated high temperature water".CORROSION SCIENCE 120(2017):219-230.