题名: Effect of Hot Isostatic Pressing Loading Route on Microstructure and Mechanical Properties of Powder Metallurgy Ti2AlNb Alloys
作者: Wu, Jie;  Guo, Ruipeng;  Xu, Lei;  Lu, Zhengguan;  Cui, Yuyou;  Yang, Rui
发表日期: 2017-2-1
摘要: In this work, hot isostatic pressing (HIPing) technique was used to densify the Ti2AlNb pre-alloyed powder. The influence of HIPing loading route parameters (temperature and rates of heating and pressurizing) on microstructure and properties of PM Ti2AlNb alloys was studied. The results showed that HIPing loading route parameters affected the densification process and mechanical properties (especially high temperature rupture lifetime) of PM Ti2AlNb alloys in the present work. A finite element method (FEM) model for predicting the final densification was developed and was used to optimize the HIPing procedure. Copyright (C) 2017, The editorial office of Journal of Materials Science & Technology. Published by Elsevier Limited.
Appears in Collections:中国科学院金属研究所_期刊论文

Files in This Item:

There are no files associated with this item.

Recommended Citation:
Wu, Jie,Guo, Ruipeng,Xu, Lei,et al. Effect Of Hot Isostatic Pressing Loading Route On Microstructure And Mechanical Properties Of Powder Metallurgy Ti2alnb Alloys[J]. Journal Of Materials Science & Technology,2017,33(2):172-178.

SCI Citaion Data:
 Recommend this item
 Sava as my favorate item
 Show this item's statistics
 Export Endnote File
Google Scholar
 Similar articles in Google Scholar
 [Wu, Jie]'s Articles
 [Guo, Ruipeng]'s Articles
 [Xu, Lei]'s Articles
CSDL cross search
 Similar articles in CSDL Cross Search
 [Wu, Jie]‘s Articles
 [Guo, Ruipeng]‘s Articles
 [Xu, Lei]‘s Articles
Scirus search
 Similar articles in Scirus
Related Copyright Policies
Social Bookmarking
  Add to CiteULike  Add to Connotea  Add to  Add to Digg  Add to Reddit 
所有评论 (0)
内 容:
Email:  *
验证码:   刷新
标 题:
内 容:
Email:  *
验证码:   刷新

Items in IR are protected by copyright, with all rights reserved, unless otherwise indicated.



Valid XHTML 1.0!
Copyright © 2007-2018  中国科学院金属研究所  -Feedback
Powered by CSpace