题名: Effects of extrusion and heat treatments on microstructure and mechanical properties of Mg-8Zn-1Al-0.5Cu-0.5Mn alloy
作者: Zhu, Shao-zhen;  Luo, Tian-jiao;  Zhang, Ting-an;  Liu, Yun-teng;  Yang, Yuan-sheng
发表日期: 2017
摘要: The effects of extrusion and heat treatments on the microstructure and mechanical properties of Mg-8Zn-1Al-0.5Cu-0.5Mn magnesium alloy were investigated. Bimodal microstructure is formed in this alloy when it is extruded at 230 and 260 degrees C, and complete DRX occurs at the extruding temperature of 290 degrees C. The basal texture of as-extruded alloys is reduced gradually with increasing extrusion temperature due to the larger volume fraction of recrystallized structure at higher temperatures. For the alloy extruded at 290 degrees C, four different heat treatments routes were investigated. After solution + aging treatments, the grains sizes become larger. Finer and far more densely dispersed precipitates are found in the alloy with solution + double-aging treatments compared with alloy with solution + single-aging treatment. Tensile properties are enhanced remarkably by solution + double-aging treatment with the yield strength, tensile strength and elongation being 298 MPa, 348 MPa and 18%, respectively. This is attributed to the combined effects of fine dynamically recrystallized grains and the uniformly distributed finer precipitates.
刊名: TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA
Appears in Collections:中国科学院金属研究所_期刊论文

Files in This Item:

There are no files associated with this item.




Recommended Citation:
Zhu, Shao-zhen,Luo, Tian-jiao,Zhang, Ting-an,et al. Effects Of Extrusion And Heat Treatments On Microstructure And Mechanical Properties Of Mg-8zn-1al-0.5cu-0.5mn Alloy[J]. Transactions Of Nonferrous Metals Society Of China,2017,27(1):73-81.

SCI Citaion Data:
Service
 Recommend this item
 Sava as my favorate item
 Show this item's statistics
 Export Endnote File
Google Scholar
 Similar articles in Google Scholar
 [Zhu, Shao-zhen]'s Articles
 [Luo, Tian-jiao]'s Articles
 [Zhang, Ting-an]'s Articles
CSDL cross search
 Similar articles in CSDL Cross Search
 [Zhu, Shao-zhen]‘s Articles
 [Luo, Tian-jiao]‘s Articles
 [Zhang, Ting-an]‘s Articles
Scirus search
 Similar articles in Scirus
Related Copyright Policies
Null
Social Bookmarking
  Add to CiteULike  Add to Connotea  Add to Del.icio.us  Add to Digg  Add to Reddit 
所有评论 (0)
暂无评论
 
评注功能仅针对注册用户开放,请您登录
您对该条目有什么异议,请填写以下表单,管理员会尽快联系您。
内 容:
Email:  *
单位:
验证码:   刷新
您在IR的使用过程中有什么好的想法或者建议可以反馈给我们。
标 题:
 *
内 容:
Email:  *
验证码:   刷新

Items in IR are protected by copyright, with all rights reserved, unless otherwise indicated.

 

 

Valid XHTML 1.0!
Copyright © 2007-2017  中国科学院金属研究所  -Feedback
Powered by CSpace